- 缺口沖擊強度: 0.374
- 拉伸強度 [MPa]: 160.0
- 彎曲模量 [MPa]: 9.51
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | Method A; ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 160 MPa | 23200 psi | ASTM D638 |
| Tensile Strength, Yield | 160 MPa | 23200 psi | ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Elongation at Yield | 1.8 % | 1.8 % | ASTM D638 |
| Tensile Modulus | 11.5 GPa | 1670 ksi | ASTM D638 |
| Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
| Flexural Modulus | 9.51 GPa | 1380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 3.18 mm | 0.701 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 4.00 J/cm @Thickness 3.18 mm | 7.49 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.30 kJ/m2 | 2.05 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 29.3 kJ/m2 | 13.9 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 4.40 J | 3.25 ft-lb | ASTM D3763 |
| Impact Test | 1.80 J | 1.33 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1000 - 1.00e+7 ohm | 1000 - 1.00e+7 ohm | ASTM D4496 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 379 - 388 °C | 714 - 730 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.010 % | 0.010 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |