- 缺口沖擊強度: 0.641
- 拉伸強度 [MPa]: 191.0
- 彎曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | Method A; ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 191 MPa | 27700 psi | ASTM D638 |
| Tensile Strength, Yield | 191 MPa | 27700 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 16.8 GPa | 2440 ksi | ASTM D638 |
| Flexural Strength | 296 MPa | 42900 psi | ASTM D790 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.18 mm | 1.20 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 6.41 J/cm @Thickness 3.18 mm | 12.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.50 kJ/m2 | 3.57 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 5.00 J | 3.69 ft-lb | ASTM D3763 |
| Impact Test | 2.30 J | 1.70 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D4496 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 379 - 388 °C | 714 - 730 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.010 % | 0.010 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |