- 密度 [g/cm3]: 1.27
- 吸水率 [%]: 0.5
- 缺口沖擊強度: 0.63
- 拉伸強度 [MPa]: 97.2
- 斷裂伸長率 [%]: 24.1
- 彎曲模量 [MPa]: 4.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in3 | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570; 24 hrs. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 97.2 MPa | 14100 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Tensile Modulus | 3.59 GPa | 520 ksi | ASTM D638 |
| Flexural Yield Strength | 24.1 MPa | 3500 psi | ASTM D790 |
| Flexural Modulus | 4.10 GPa | 594 ksi | ASTM D790 |
| Izod Impact, Notched | 0.630 J/cm | 1.18 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.2 @Frequency 1000 Hz | 3.2 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 46.8 μm/m-°C @Temperature 20.0 °C | 26.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 340 °C | 644 °F | ASTM D4591 |
| Maximum Service Temperature, Air | 240 °C | 464 °F | Continuous Use |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 35 % | 35 % | ASTM D2863 |