- 密度 [g/cm3]: 1.256
- 吸水率 [%]: 0.4
- 彎曲模量 [MPa]: 3.66
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.256 g/cc | 0.04538 lb/in3 | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570; 24 hrs. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 120 MPa | 17400 psi | ASTM D882 |
| Elongation at Break | 50 % | 50 % | ASTM D882 |
| Tensile Modulus | 2.699 GPa | 391.5 ksi | ASTM D882 |
| Flexural Modulus | 3.66 GPa | 531 ksi | ASTM D790 |
| Tear Strength | 13.7 kN/m | 78.4 pli | ASTM D1004 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.80e+15 ohm | 1.80e+15 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1000 Hz | 3.3 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 126 kV/mm @Thickness 0.0762 mm | 3200 kV/in @Thickness 0.00300 in | ASTM D149 |
| Dissipation Factor | 0.0026 @Frequency 10000 Hz | 0.0026 @Frequency 10000 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 340 °C | 644 °F | DSC |
| Maximum Service Temperature, Air | 240 °C | 464 °F | Continuous Use |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 330 °F | ASTM D648 |
| Glass Transition Temp, Tg | 142.7 °C | 288.9 °F | ASTM D3418 |
| Flammability, UL94 | V-0 | V-0 | VTM-1 |
| NBS Smoke Density | <= 1.0 | <= 1.0 | ASTM E662 |
| Oxygen Index | 23 % | 23 % | ASTM D2863 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.50 % | 0.50 % | ASTM D1003 |