- 密度 [g/cm3]: 1.26
- 吸水率 [%]: 0.4
- 缺口沖擊強(qiáng)度: 9.5
- 拉伸強(qiáng)度 [MPa]: 95.0
- 彎曲模量 [MPa]: 4.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in3 | Amorphous; ISO 1183 | ||
| 1.30 g/cc | 0.0470 lb/in3 | Crystalline; ISO 1183 | |||
| Water Absorption | 0.40 % | 0.40 % | by immersion; ISO 62-1 | ||
| 0.070 % @Time 86400 sec | 0.070 % @Time 24.0 hour | 3.2 mm thick Tensile bar; ISO 62-1 | |||
| Viscosity | 500000 cP @Temperature 400 °C | 500000 cP @Temperature 752 °F | Melt; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | 390°C nozzle, 200°C tool; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | 390°C nozzle, 200°C tool; ISO 294-4 | ||
| Spiral Flow | 12.5 cm @Thickness 1.00 mm | 4.92 in @Thickness 0.0394 in | 390°C nozzle, 180°C tool; Victrex | ||
| 63.0 cm @Thickness 76.2 mm | 24.8 in @Thickness 3.00 in | 395°C nozzle, 180°C tool; Victrex | |||
| 70.0 cm @Thickness 76.2 mm | 27.6 in @Thickness 3.00 in | 415°C nozzle, 180°C tool; Victrex | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 84 | 84 | ISO 868 | ||
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 | ||
| Elongation at Break | 45 % | 45 % | ISO 527 | ||
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527 | ||
| Flexural Strength | 9.00 MPa @Temperature 275 °C | 1310 psi @Temperature 527 °F | ISO 178 | ||
| 16.0 MPa @Temperature 175 °C | 2320 psi @Temperature 347 °F | ISO 178 | |||
| 85.0 MPa @Temperature 125 °C | 12300 psi @Temperature 257 °F | ISO 178 | |||
| 155 MPa @Temperature 23.0 °C | 22500 psi @Temperature 73.4 °F | ISO 178 | |||
| Flexural Modulus | 4.00 GPa | 580 ksi | ISO 178 | ||
| Compressive Strength | 65.0 MPa @Temperature 120 °C | 9430 psi @Temperature 248 °F | ISO 604 | ||
| 120 MPa @Temperature 23.0 °C | 17400 psi @Temperature 73.4 °F | ISO 604 | |||
| Izod Impact, Notched (ISO) | 9.50 kJ/m2 | 4.52 ft-lb/in2 | ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/U | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/U | ||
| Charpy Impact, Notched | 0.0800 J/cm2 | 0.381 ft-lb/in2 | ISO 179/eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+9 ohm-cm @Temperature 275 °C | 1.00e+9 ohm-cm @Temperature 527 °F | |||
| 1.00e+15 ohm-cm @Temperature 125 °C | 1.00e+15 ohm-cm @Temperature 257 °F | ||||
| 1.00e+16 ohm-cm @Temperature 23.0 °C | 1.00e+16 ohm-cm @Temperature 73.4 °F | ||||
| Dielectric Constant | 3.1 @Frequency 50000 Hz, Temperature 23.0 °C | 3.1 @Frequency 50000 Hz, Temperature 73.4 °F | |||
| Dielectric Strength | 20.0 kV/mm @Thickness 2.50 mm | 508 kV/in @Thickness 0.0984 in | IEC 60243-1 | ||
| Dissipation Factor | 0.0050 @Frequency 1.00e+6 Hz | 0.0050 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 45.0 μm/m-°C | 25.0 μin/in-°F | Along flow below Tg; ISO 11359 | ||
| 125 μm/m-°C | 69.4 μin/in-°F | Along flow above Tg; ISO 11359 | |||
| CTE, linear, Transverse to Flow | 65.0 μm/m-°C | 36.1 μin/in-°F | Average below Tg; ISO 11359 | ||
| 160 μm/m-°C | 88.9 μin/in-°F | Average above Tg; ISO 11359 | |||
| Specific Heat Capacity | 2.20 J/g-°C | 0.526 BTU/lb-°F | DSC | ||
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft2-°F | ISO/CD 22007-4 | ||
| Melting Point | 343 °C | 649 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ISO 75-f | ||
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 | ||
| Oxygen Index | 24 % @Thickness 0.400 mm | 24 % @Thickness 0.0157 in | ISO 4589 | ||
| 35 % @Thickness 3.20 mm | 35 % @Thickness 0.126 in | ISO 4589 | |||
| Glow Wire Test | 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature | ||
| Nozzle Temperature | 395 °C | 743 °F | |||
| Zone 1 | 375 °C | 707 °F | |||
| Zone 2 | 380 °C | 716 °F | |||
| Zone 3 | 385 °C | 725 °F | |||
| Zone 4 | 390 °C | 734 °F | |||
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |||
| <= 250 °C | <= 482 °F | ||||
| Dry Time | 3 hour @Temperature 150 °C | 3 hour @Temperature 302 °F | |||
| 5 hour @Temperature 120 °C | 5 hour @Temperature 248 °F | ||||
| Component Elements Properties | Metric | English | Comments | ||
| CO2 | 0.15 % | 0.15 % | NES 713 | ||
| Descriptive Properties | |||||
| CO | 0.074 | NES 713 | |||
| Color | Natural/Beige | ||||
| Gate | > 1mm or 0.5 x part thickness | ||||
| Runner | Die/nozzle > 3mm, manifold > 3.5mm | ||||
| Total gases | 0.22 | NES 713 | |||