- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.04
- 缺口沖擊強度: 0.6
- 彎曲模量 [MPa]: 24.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | Crystalline; ISO 1183 | ||
| Water Absorption | 0.040 % @Temperature 23.0 °C, Time 86400 sec | 0.040 % @Temperature 73.4 °F, Time 24.0 hour | 3.2mm thick tensile bar; ISO 62-1 | ||
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C | 0.30 % @Temperature 73.4 °F | Equilibrium; by immersion; ISO 62-1 | ||
| Viscosity | 260000 cP @Temperature 400 °C | 260000 cP @Temperature 752 °F | melt; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | 360°C nozzle, 160°C tool; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | 380°C nozzle, 190°C tool; ISO 294-4 | ||
| Spiral Flow | 130 cm @Thickness 1.00 mm | 51.2 in @Thickness 0.0394 in | 380°C nozzle, 190°C tool | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 91 @Temperature 23.0 °C | 91 @Temperature 73.4 °F | ISO 868 | ||
| Tensile Strength at Break | 65.0 MPa @Temperature 275 °C | 9430 psi @Temperature 527 °F | ISO 527 | ||
| 85.0 MPa @Temperature 225 °C | 12300 psi @Temperature 437 °F | ISO 527 | |||
| 110 MPa @Temperature 175 °C | 16000 psi @Temperature 347 °F | ISO 527 | |||
| 180 MPa @Temperature 125 °C | 26100 psi @Temperature 257 °F | ISO 527 | |||
| 260 MPa @Temperature 23.0 °C | 37700 psi @Temperature 73.4 °F | ISO 527 | |||
| Elongation at Break | 1.3 % @Temperature 23.0 °C | 1.3 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 27.0 GPa @Temperature 23.0 °C | 3920 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 60.0 MPa @Temperature 225 °C | 8700 psi @Temperature 437 °F | ISO 178 | ||
| 120 MPa @Temperature 175 °C | 17400 psi @Temperature 347 °F | ISO 178 | |||
| 250 MPa @Temperature 125 °C | 36300 psi @Temperature 257 °F | ISO 178 | |||
| 360 MPa @Temperature 23.0 °C | 52200 psi @Temperature 73.4 °F | ISO 178 | |||
| Flexural Modulus | 24.0 GPa @Temperature 23.0 °C | 3480 ksi @Temperature 73.4 °F | ISO 178 | ||
| Compressive Strength | 70.0 MPa @Temperature 200 °C | 10200 psi @Temperature 392 °F | ISO 604 | ||
| 200 MPa @Temperature 120 °C | 29000 psi @Temperature 248 °F | ISO 604 | |||
| 300 MPa @Temperature 23.0 °C | 43500 psi @Temperature 73.4 °F | ISO 604 | |||
| Izod Impact, Notched (ISO) | 0.600 kJ/m2 @Temperature 23.0 °C | 0.286 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | 3.50 kJ/m2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | ISO 180/U | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 5.00 μm/m-°C @Temperature <=143 °C | 2.78 μin/in-°F @Temperature <=289 °F | Along flow below Tg; ISO 11359 | ||
| 5.00 μm/m-°C @Temperature >=143 °C | 2.78 μin/in-°F @Temperature >=289 °F | Along flow above Tg; ISO 11359 | |||
| 40.0 μm/m-°C @Temperature <=143 °C | 22.2 μin/in-°F @Temperature <=289 °F | Average below Tg; ISO 11359 | |||
| 90.0 μm/m-°C @Temperature >=143 °C | 50.0 μin/in-°F @Temperature >=289 °F | Average above Tg; ISO 11359 | |||
| Specific Heat Capacity | 1.80 J/g-°C @Temperature 23.0 °C | 0.430 BTU/lb-°F @Temperature 73.4 °F | DSC | ||
| Thermal Conductivity | 0.960 W/m-K @Temperature 23.0 °C | 6.66 BTU-in/hr-ft2-°F @Temperature 73.4 °F | ISO/CD 22007-4 | ||
| Melting Point | 343 °C | 649 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 342 °C | 648 °F | ISO 75A-f | ||
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 | ||
| Flammability, UL94 | V-0 @Thickness 0.500 mm | V-0 @Thickness 0.0197 in | |||
| Glow Wire Test | 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |||
| Drying Temperature | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |||
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour | ||||
| Descriptive Properties | |||||
| Toxicity Index | 0.05 | NES 713; CO content | |||
| 0.12 | NES 713; CO2 content | ||||
| 0.17 | NES 713; Total gases | ||||