- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.05
- 缺口沖擊強度: 0.7
- 彎曲模量 [MPa]: 8.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | Crystalline; ISO 1183 |
| Water Absorption | 0.050 % @Temperature 23.0 °C, Time 86400 sec | 0.050 % @Temperature 73.4 °F, Time 24.0 hour | 3.2mm thick tensile bar; ISO 62-1 |
| Water Absorption at Saturation | 0.40 % @Temperature 23.0 °C | 0.40 % @Temperature 73.4 °F | Equilibrium; by immersion; ISO 62-1 |
| Viscosity | 230000 cP @Temperature 400 °C | 230000 cP @Temperature 752 °F | melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | 380°C nozzle, 180°C tool; ISO 294-4 |
| Spiral Flow | 160 cm @Thickness 1.00 mm | 63.0 in @Thickness 0.0394 in | 380°C nozzle, 180°C tool |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 145 MPa @Temperature 23.0 °C | 21000 psi @Temperature 73.4 °F | ISO 527 |
| Elongation at Break | 2.4 % @Temperature 23.0 °C | 2.4 % @Temperature 73.4 °F | ISO 527 |
| Tensile Modulus | 9.00 GPa @Temperature 23.0 °C | 1310 ksi @Temperature 73.4 °F | ISO 527 |
| Flexural Strength | 240 MPa @Temperature 23.0 °C | 34800 psi @Temperature 73.4 °F | ISO 178 |
| Flexural Modulus | 8.50 GPa @Temperature 23.0 °C | 1230 ksi @Temperature 73.4 °F | ISO 178 |
| Izod Impact, Notched (ISO) | 0.700 kJ/m2 @Temperature 23.0 °C | 0.333 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A |
| Izod Impact, Unnotched (ISO) | 3.50 kJ/m2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | ISO 180/U |
| Charpy Impact Unnotched | 3.50 J/cm2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1U |
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1000 Hz, Temperature 23.0 °C | 3.2 @Frequency 1000 Hz, Temperature 73.4 °F | IEC 60250 |
| Dielectric Strength | 17.0 kV/mm @Thickness 2.50 mm | 432 kV/in @Thickness 0.0984 in | IEC 60243-1 |
| Dissipation Factor | 0.0040 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.0040 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 25.0 μm/m-°C @Temperature <=143 °C | 13.9 μin/in-°F @Temperature <=289 °F | Along flow below Tg; ISO 11359 |
| 25.0 μm/m-°C @Temperature >=143 °C | 13.9 μin/in-°F @Temperature >=289 °F | Along flow above Tg; ISO 11359 | |
| 45.0 μm/m-°C @Temperature <=143 °C | 25.0 μin/in-°F @Temperature <=289 °F | Average below Tg; ISO 11359 | |
| 130 μm/m-°C @Temperature >=143 °C | 72.2 μin/in-°F @Temperature >=289 °F | Average above Tg; ISO 11359 | |
| Specific Heat Capacity | 1.70 J/g-°C @Temperature 23.0 °C | 0.406 BTU/lb-°F @Temperature 73.4 °F | DSC |
| Thermal Conductivity | 0.300 W/m-K @Temperature 23.0 °C | 2.08 BTU-in/hr-ft2-°F @Temperature 73.4 °F | ISO/CD 22007-4 |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 323 °C | 613 °F | ISO 75-f |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| Flammability, UL94 | V-0 @Thickness 0.500 mm | V-0 @Thickness 0.0197 in | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour | ||