- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.05
- 缺口沖擊強度: 0.8
- 彎曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | Crystalline; ISO 1183 | ||
| Water Absorption | 0.050 % @Temperature 23.0 °C, Time 86400 sec | 0.050 % @Temperature 73.4 °F, Time 24.0 hour | 3.2mm thick tensile bar; ISO 62-1 | ||
| Water Absorption at Saturation | 0.40 % @Temperature 23.0 °C | 0.40 % @Temperature 73.4 °F | Equilibrium; by immersion; ISO 62-1 | ||
| Viscosity | 550000 cP @Temperature 400 °C | 550000 cP @Temperature 752 °F | melt; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | 360°C nozzle, 160°C tool; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | 395°C nozzle, 200°C tool; ISO 294-4 | ||
| Spiral Flow | 100 cm @Thickness 1.00 mm | 39.4 in @Thickness 0.0394 in | 395°C nozzle, 200°C tool | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 90 @Temperature 23.0 °C | 90 @Temperature 73.4 °F | ISO 868 | ||
| Tensile Strength at Break | 210 MPa @Temperature 23.0 °C | 30500 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.1 % @Temperature 23.0 °C | 2.1 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 18.0 GPa @Temperature 23.0 °C | 2610 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 310 MPa @Temperature 23.0 °C | 45000 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 16.0 GPa @Temperature 23.0 °C | 2320 ksi @Temperature 73.4 °F | ISO 178 | ||
| Izod Impact, Notched (ISO) | 0.800 kJ/m2 @Temperature 23.0 °C | 0.381 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | 4.50 kJ/m2 @Temperature 23.0 °C | 2.14 ft-lb/in2 @Temperature 73.4 °F | ISO 180/U | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.80 J/g-°C @Temperature 23.0 °C | 0.430 BTU/lb-°F @Temperature 73.4 °F | DSC | ||
| Thermal Conductivity | 0.950 W/m-K @Temperature 23.0 °C | 6.59 BTU-in/hr-ft2-°F @Temperature 73.4 °F | ISO/CD 22007-4 | ||
| Melting Point | 343 °C | 649 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 325 °C | 617 °F | ISO 75-f | ||
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 | ||
| Flammability, UL94 | V-0 @Thickness 0.500 mm | V-0 @Thickness 0.0197 in | |||
| Glow Wire Test | 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 180 - 210 °C | 356 - 410 °F | |||
| Drying Temperature | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |||
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour | ||||
| Descriptive Properties | |||||
| Toxicity Index | 0.05 | NES 713; CO content | |||
| 0.12 | NES 713; CO2 content | ||||
| 0.17 | NES 713; Total gases | ||||