- 密度 [g/cm3]: 1.37
- 缺口沖擊強度: 0.961
- 拉伸強度 [MPa]: 74.5
- 彎曲模量 [MPa]: 2.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | Method A; ASTM D792 |
| Density | 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 69.6 MPa | 10100 psi | ASTM D638 |
| Tensile Strength, Yield | 74.5 MPa | 10800 psi | ASTM D638 |
| Elongation at Break | 23 % | 23 % | ASTM D638 |
| Elongation at Yield | 5.8 % | 5.8 % | ASTM D638 |
| Tensile Modulus | 2.90 GPa | 421 ksi | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 2.96 GPa | 429 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.18 mm | 1.80 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 15.5 J/cm @Thickness 3.18 mm | 29.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.80 kJ/m2 | 4.19 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 91.2 kJ/m2 | 43.4 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 2.80 J | 2.07 ft-lb | ASTM D3763 |
| Impact Test | 1.35 J | 0.996 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Coefficient of Friction, Dynamic | 0.52 | 0.52 | vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894 |
| Coefficient of Friction, Static | 0.43 | 0.43 | vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894 |
| K (wear) Factor | 258 x 10-8 mm3/N-M | 128 x 10-10 in3-min/ft-lb-hr | 40psi, 50ft/min; tested in accordance with LNP WI-0687 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 379 - 388 °C | 714 - 730 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.10 % | 0.10 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |