- 吸水率 [%]: 0.5
- 拉伸強度 [MPa]: 95.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ISO 1183 |
| Water Absorption | 0.50 % | 0.50 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 95.1 MPa | 13800 psi | ISO 527 |
| 114.0 MPa | 16530 psi | Extruded Rod; ISO 527 | |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ISO 527 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistivity per Square | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 33.3 μin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 |
| Vicat Softening Point | 335 °C @Load 1.02 kg | 635 °F @Load 2.25 lb | Method A; ISO 306 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 340 °C | 644 °F | DSC, Second Heating; ISO 11357 |