- 缺口沖擊強度: 0.427
- 彎曲模量 [MPa]: 20.1
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength at Break | 194 MPa | 28100 psi | ASTM D638 | ||
| Flexural Modulus | 20.1 GPa | 2920 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.18 mm | 0.800 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| Izod Impact, Unnotched | 4.27 J/cm @Thickness 3.18 mm | 8.00 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 379 - 388 °C | 714 - 730 °F | |||
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |||
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.010 % | 0.010 % | Suggested | ||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |||
| Descriptive Properties | |||||
| Color | Black | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.