- 缺口沖擊強(qiáng)度: 0.641
- 拉伸強(qiáng)度 [MPa]: 228.0
- 彎曲模量 [MPa]: 21.6
- 熱變形溫度 [℃]: 300.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | Method A; ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 228 MPa | 33100 psi | ASTM D638 |
| Tensile Strength, Yield | 228 MPa | 33100 psi | ASTM D638 |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| Elongation at Yield | 1.3 % | 1.3 % | ASTM D638 |
| Tensile Modulus | 25.0 GPa | 3630 ksi | ASTM D638 |
| Flexural Strength | 338 MPa | 49000 psi | ASTM D790 |
| Flexural Modulus | 21.6 GPa | 3130 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.18 mm | 1.20 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 4.32 J/cm @Thickness 3.18 mm | 8.09 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 37.4 kJ/m2 | 17.8 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 7.62 J | 5.62 ft-lb | ASTM D3763 |
| Impact Test | 4.57 J | 3.37 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 μm/m-°C @Temperature 20.0 °C | 10.0 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| CTE, linear, Transverse to Flow | 32.0 μm/m-°C @Temperature 20.0 °C | 17.8 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 300 °C | 572 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 379 - 388 °C | 714 - 730 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.10 % | 0.10 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |