- 缺口沖擊強度: 0.747
- 拉伸強度 [MPa]: 225.0
- 彎曲模量 [MPa]: 20.2
- 熱變形溫度 [℃]: 299.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | Method A; ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 225 MPa | 32600 psi | ASTM D638 |
| Tensile Strength, Yield | 225 MPa | 32600 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Elongation at Yield | 1.4 % | 1.4 % | ASTM D638 |
| Tensile Modulus | 30.8 GPa | 4470 ksi | ASTM D638 |
| Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
| Flexural Modulus | 20.2 GPa | 2930 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.18 mm | 1.40 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 6.09 J/cm @Thickness 3.18 mm | 11.4 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.80 kJ/m2 | 3.71 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 42.6 kJ/m2 | 20.3 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 12.5 J | 9.22 ft-lb | ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894 |
| Coefficient of Friction, Static | 0.32 | 0.32 | vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894 |
| K (wear) Factor | 111 x 10-8 mm3/N-M | 55.0 x 10-10 in3-min/ft-lb-hr | 40psi, 50ft/min; tested in accordance with LNP WI-0687 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.0 μm/m-°C @Temperature 20.0 °C | 6.11 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| CTE, linear, Transverse to Flow | 29.0 μm/m-°C @Temperature 20.0 °C | 16.1 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 299 °C | 570 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 299 °C | 570 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.770 mm | V-0 @Thickness 0.0303 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 379 - 388 °C | 714 - 730 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.10 % | 0.10 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |