- 吸水率 [%]: 0.1
- 缺口沖擊強度: 1.7
- 斷裂伸長率 [%]: 134
- 彎曲模量 [MPa]: 3.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 | ||
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 | ||
| Viscosity | 170 cP @Shear Rate 1000 1/s, Temperature 400 °C | 170 cP @Shear Rate 1000 1/s, Temperature 752 °F | Melt; ASTM D3835 | ||
| Linear Mold Shrinkage, Flow | 0.012 - 0.014 cm/cm @Thickness 3.20 mm | 0.012 - 0.014 in/in @Thickness 0.126 in | 5" x 0.5" x 0.125" bars; ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.016 - 0.018 cm/cm @Thickness 3.20 mm | 0.016 - 0.018 in/in @Thickness 0.126 in | 5" x 0.5" x 0.125" bar; ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 83 @Time 1.00 sec | 83 @Time 0.000278 hour | ASTM D2240 | ||
| Tensile Strength | 88.0 MPa | 12800 psi | 50 mm/min; ASTM D638 | ||
| Elongation at Break | 60 % | 60 % | 50 mm/min; ASTM D638 | ||
| 60 % | 60 % | ISO 527-2/1A/50 | |||
| Elongation at Yield | 5.2 % | 5.2 % | 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 3.60 GPa | 522 ksi | 50 mm/min; ASTM D638 | ||
| Flexural Strength | 134 MPa | 19400 psi | ASTM D790 | ||
| Flexural Yield Strength | 134 MPa | 19400 psi | ASTM D790 | ||
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 | ||
| NB | NB | ASTM D4812 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | Annealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 365 °C | 689 °F | |||
| Middle Barrel Temperature | 370 °C | 698 °F | |||
| Front Barrel Temperature | 375 °C | 707 °F | |||
| Nozzle Temperature | 380 °C | 716 °F | |||
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Black | ||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Fatigue Resistant | ||||
| Flame Retardant | |||||
| Good Chemical Resistance | |||||
| Good Dimensional Stability | |||||
| Good Wear Resistance | |||||
| High Heat Resistance | |||||
| Forms | Pellets | ||||
| Generic | PEEK | ||||
| Injection Rate | Fast | ||||
| Processing Method | Injection Molding | ||||
| Machining | |||||
| Profile Extrusion | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | ||||
| Uses | Film | ||||
| Industrial Applications | |||||
| Oil/Gas Applications | |||||
| Profiles | |||||
| Rods | |||||
| Sheet | |||||
| Tubing | |||||