- 密度 [g/cm3]: 1.62
- 缺口沖擊強度: 10.0
- 斷裂伸長率 [%]: 178
- 彎曲模量 [MPa]: 8.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.021 - 0.023 cm/cm | 0.021 - 0.023 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| Flexural Yield Strength | 178 MPa | 25800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 18.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 10.0 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 46.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 25.6 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |