- 缺口沖擊強度: 0.91
- 彎曲模量 [MPa]: 5.60
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 | ||
| Filler Content | 13 % | 13 % | Glass Fiber Reinforcement | ||
| Viscosity | 534000 cP @Shear Rate 1000 1/s, Temperature 400 °C | 534000 cP @Shear Rate 1000 1/s, Temperature 752 °F | Melt; Internal Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 117 MPa | 17000 psi | ASTM D638 | ||
| Elongation at Break | 6.2 % | 6.2 % | ASTM D638 | ||
| Elongation at Yield | 3.9 % | 3.9 % | ASTM D638 | ||
| Tensile Modulus | 5.90 GPa | 856 ksi | ASTM D638 | ||
| Flexural Strength | 203 MPa | 29400 psi | ASTM D790 | ||
| Flexural Modulus | 5.60 GPa | 812 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 | ||
| 10.0 J/cm | 18.7 ft-lb/in | ASTM D4218 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 365 °C | 689 °F | |||
| Middle Barrel Temperature | 370 °C | 698 °F | |||
| Front Barrel Temperature | 375 °C | 707 °F | |||
| Nozzle Temperature | 380 °C | 716 °F | |||
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Beige | ||||
| Opaque | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Fatigue Resistant | ||||
| Flame Retardant | |||||
| Good Chemical Resistance | |||||
| Good Dimensional Stability | |||||
| High Heat Resistance | |||||
| High Stiffness | |||||
| High Strength | |||||
| Forms | Pellets | ||||
| Powder | |||||
| Generic | PEEK | ||||
| Injection Rate | Fast | ||||
| Processing Method | Injection Molding | ||||
| Machining | |||||
| Profile Extrusion | |||||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | ||||
| Uses | Industrial Applications | ||||
| Medical/Healthcare Applications | |||||
| Oil/Gas Applications | |||||