- 密度 [g/cm3]: 1.45
- 缺口沖擊強度: 0.85
- 彎曲模量 [MPa]: 8.31
- 熱變形溫度 [℃]: 242.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D 792 |
| Density | 1.45 g/cc | 0.0524 lb/in3 | ASTM D 792 |
| 1.46 g/cc | 0.0527 lb/in3 | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.19 % @Time 86400 sec | 0.19 % @Time 24.0 hour | 50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec | 0.0030 - 0.0060 in/in @Time 24.0 hour | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm @Time 86400 sec | 0.0070 - 0.010 in/in @Time 24.0 hour | ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 151 MPa | 21900 psi | Type I, 5 mm/min; ASTM D 638 |
| 152 MPa | 22000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.4 % | 5.4 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 14.19 GPa | 2058 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 223 MPa | 32300 psi | brk, 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 8.31 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 9.64 GPa | 1400 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm @Temperature 23.0 °C | 1.59 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 8.72 J/cm @Temperature 23.0 °C | 16.3 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 54.0 kJ/m2 @Temperature 23.0 °C | 25.7 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 242 °C | 468 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 280 °C @Thickness 3.20 mm | 536 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C @Thickness 3.20 mm | 532 °F @Thickness 0.126 in | unannealed; ASTM D 648 |