- 密度 [g/cm3]: 1.4
- 缺口沖擊強度: 0.64
- 彎曲模量 [MPa]: 21.64
- 熱變形溫度 [℃]: 300.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ISO 1183 |
| 1.41 g/cc | 0.0509 lb/in3 | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C / 50% RH; ISO 62 |
| 0.060 % @Time 86400 sec | 0.060 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec | 0.0010 in/in @Time 24.0 hour | ASTM D 955 |
| 0.0011 cm/cm @Time 86400 sec | 0.0011 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0077 cm/cm @Time 86400 sec | 0.0077 in/in @Time 24.0 hour | ISO 294 |
| 0.0080 cm/cm @Time 86400 sec | 0.0080 in/in @Time 24.0 hour | ASTM D 955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 227 MPa | 32900 psi | ASTM D 638 |
| 228 MPa | 33100 psi | ISO 527 | |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527 |
| 1.3 % | 1.3 % | ASTM D 638 | |
| Tensile Modulus | 24.56 GPa | 3562 ksi | 1 mm/min; ISO 527 |
| 24.95 GPa | 3619 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 340 MPa | 49300 psi | ISO 178 |
| 340 MPa | 49300 psi | ASTM D 790 | |
| Flexural Modulus | 21.64 GPa | 3139 ksi | ASTM D 790 |
| 21.65 GPa | 3140 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C | 1.20 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 4.32 J/cm @Temperature 23.0 °C | 8.09 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m2 @Temperature 23.0 °C | 17.6 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C | 5.16 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 18.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 10.0 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 18.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 10.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 34.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 18.9 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 34.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 18.9 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 300 °C @Thickness 3.20 mm | 572 °F @Thickness 0.126 in | unannealed; ASTM D 648 |