- 密度 [g/cm3]: 1.4
- 缺口沖擊強(qiáng)度: 9.0
- 斷裂伸長率 [%]: 301
- 彎曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 219 MPa | 31800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 23.4 GPa | 3390 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 301 MPa | 43700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 17.0 GPa | 2470 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 6.90 μm/m-°C @Temperature 23.0 - 60.0 °C | 3.83 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 42.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 23.3 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL 94 |