- 密度 [g/cm3]: 1.34
- 缺口沖擊強(qiáng)度: 5.0
- 拉伸強(qiáng)度 [MPa]: 200.0
- 斷裂伸長(zhǎng)率 [%]: 275
- 彎曲模量 [MPa]: 11.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 200 MPa | 29000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 3.1 % | 3.1 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 13.8 GPa | 2000 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 275 MPa | 39900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 11.1 GPa | 1610 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m2 | 14.3 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 10000 - 1.00e+7 ohm | 10000 - 1.00e+7 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 10.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 5.56 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 54.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 30.0 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 300 °C | 572 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |