- 密度 [g/cm3]: 1.37
- 缺口沖擊強(qiáng)度: 0.96
- 拉伸強(qiáng)度 [MPa]: 73.0
- 彎曲模量 [MPa]: 2.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.0600 % | 0.0600 % | 50% RH, 24 hrs; ASTM D570 |
| 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Time 86400 sec | 0.013 in/in @Time 24.0 hour | ASTM D955 |
| 0.013 cm/cm @Time 86400 sec | 0.013 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0185 cm/cm @Time 86400 sec | 0.0185 in/in @Time 24.0 hour | ISO 294 |
| 0.019 cm/cm @Time 86400 sec | 0.019 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 69.0 MPa | 10000 psi | ASTM D638 |
| 69.0 MPa | 10000 psi | ISO 527 | |
| Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527 |
| 74.0 MPa | 10700 psi | ASTM D638 | |
| Elongation at Break | 11.8 % | 11.8 % | ISO 527 |
| 23.3 % | 23.3 % | ASTM D638 | |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 |
| 5.8 % | 5.8 % | ASTM D638 | |
| Tensile Modulus | 2.89 GPa | 419 ksi | 50 mm/min; ASTM D638 |
| 3.06 GPa | 444 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| 118 MPa | 17100 psi | ISO 178 | |
| Flexural Modulus | 2.96 GPa | 429 ksi | ASTM D790 |
| 3.32 GPa | 482 ksi | ISO 178 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.53 J/cm | 29.09 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m2 | 3.81 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 91.0 kJ/m2 | 43.3 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J | 1.48 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.52 | 0.52 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.43 | 0.43 | ASTM D3702 Modified |
| K (wear) Factor | 258 x 10-8 mm3/N-M | 128 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |