- 密度 [g/cm3]: 1.45
- 缺口沖擊強度: 9.0
- 彎曲模量 [MPa]: 22.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 256 MPa | 37100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 26.2 GPa | 3800 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 341 MPa | 49500 psi | break, 2 mm/min; ISO 178 |
| Flexural Modulus | 22.9 GPa | 3320 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 4.00 μm/m-°C @Temperature 23.0 - 60.0 °C | 2.22 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 41.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 22.8 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |