- 密度 [g/cm3]: 1.52
- 缺口沖擊強度: 0.55
- 拉伸強度 [MPa]: 111.0
- 斷裂伸長率 [%]: 179
- 彎曲模量 [MPa]: 6.85
- 熱變形溫度 [℃]: 315.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in3 | ISO 1183 |
| 1.53 g/cc | 0.0553 lb/in3 | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.080 % | 0.080 % | 23°C / 50% RH; ISO 62 |
| 0.060 % @Time 86400 sec | 0.060 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec | 0.0040 - 0.0070 in/in @Time 24.0 hour | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm @Time 86400 sec | 0.0060 - 0.0090 in/in @Time 24.0 hour | ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
| 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
| 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 7.11 GPa | 1030 ksi | 50 mm/min; ASTM D 638 |
| 7.72 GPa | 1120 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 178 MPa | 25800 psi | brk, 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 179 MPa | 26000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 6.85 GPa | 994 ksi | 2 mm/min; ISO 178 |
| 7.22 GPa | 1050 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.550 J/cm @Temperature 23.0 °C | 1.03 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 7.05 J/cm @Temperature 23.0 °C | 13.2 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| 8.00 J @Temperature 23.0 °C | 5.90 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 30.6 μm/m-°C @Temperature -30.0 - 30.0 °C | 17.0 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| CTE, linear, Transverse to Flow | 36.5 μm/m-°C @Temperature -30.0 - 30.0 °C | 20.3 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 315 °C | 599 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 156 °C @Thickness 3.20 mm | 313 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |