- 熔體流動(dòng)速率 [g/10min]: 0.7
- 吸水率 [%]: 0.1
- 缺口沖擊強(qiáng)度: 1.1
- 拉伸強(qiáng)度 [MPa]: 158.0
- 斷裂伸長率 [%]: 261
- 彎曲模量 [MPa]: 10.4
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 | ||
| Filler Content | 30 % | 30 % | Glass Fiber Reinforcement | ||
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 | ||
| Viscosity | 850000 cP @Shear Rate 1000 1/s, Temperature 400 °C | 850000 cP @Shear Rate 1000 1/s, Temperature 752 °F | Melt; ASTM D3835 | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.18 mm | 0.0020 - 0.0040 in/in @Thickness 0.125 in | 5" x 0.5" x 0.125"; ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Thickness 3.18 mm | 0.014 - 0.016 in/in @Thickness 0.125 in | 5" x 0.5" x 0.125"; ASTM D955 | ||
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 400 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 752 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 100 | 100 | M-Scale; ASTM D785 | ||
| Hardness, Shore D | 91 @Time 1.00 sec | 91 @Time 0.000278 hour | ASTM D2240 | ||
| Tensile Strength | 158 MPa | 22900 psi | ASTM D638 | ||
| Tensile Strength, Yield | 158 MPa | 22900 psi | 5.0 mm/min; ASTM D638 | ||
| 165 MPa | 23900 psi | ISO 527-2/1A/5 | |||
| Elongation at Break | 2.7 % | 2.7 % | 5.0 mm/min; ASTM D638 | ||
| 2.7 % | 2.7 % | ISO 527-2/1A/5 | |||
| Tensile Modulus | 10.5 GPa | 1520 ksi | 5.0 mm/min; ASTM D638 | ||
| 11.4 GPa | 1650 ksi | ISO 527-2/1A/1 | |||
| Flexural Strength | 246 MPa | 35700 psi | ISO 178 | ||
| 261 MPa | 37900 psi | ASTM D790 | |||
| Flexural Yield Strength | 261 MPa | 37900 psi | ASTM D790 | ||
| Flexural Modulus | 10.4 GPa | 1510 ksi | ASTM D790 | ||
| 10.7 GPa | 1550 ksi | ISO 178 | |||
| Compressive Strength | 169 MPa | 24500 psi | ASTM D695 | ||
| Poissons Ratio | 0.34 | 0.34 | ASTM E132 | ||
| Shear Modulus | 3.92 - 4.25 GPa | 569 - 616 ksi | Calculated | ||
| Shear Strength | 93.1 MPa | 13500 psi | ASTM D732 | ||
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 | ||
| 9.60 J/cm | 18.0 ft-lb/in | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 13.0 kJ/m2 | 6.19 ft-lb/in2 | ISO 180 | ||
| Izod Impact, Unnotched (ISO) | 56.0 kJ/m2 | 26.6 ft-lb/in2 | ISO 180 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.90e+17 ohm-cm | 1.90e+17 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 | ||
| Dielectric Constant | 3.41 @Frequency 1.00e+6 Hz | 3.41 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.44 @Frequency 1000 Hz | 3.44 @Frequency 1000 Hz | ASTM D150 | |||
| 3.44 @Frequency 60.0 Hz | 3.44 @Frequency 60.0 Hz | ASTM D150 | |||
| Dielectric Strength | 0.669 kV/mm @Thickness 3.00 mm | 17.0 kV/in @Thickness 0.118 in | ASTM D149 | ||
| Dissipation Factor | 0.0010 @Frequency 1000 Hz | 0.0010 @Frequency 1000 Hz | ASTM D150 | ||
| 0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | ASTM D150 | |||
| 0.0030 @Frequency 1.00e+6 Hz | 0.0030 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 17.0 μm/m-°C @Temperature -50.0 - 50.0 °C | 9.44 μin/in-°F @Temperature -58.0 - 122 °F | TMA; ASTM E831 | ||
| Specific Heat Capacity | 1.30 J/g-°C @Temperature 50.0 °C | 0.311 BTU/lb-°F @Temperature 122 °F | DSC | ||
| 1.73 J/g-°C @Temperature 200 °C | 0.413 BTU/lb-°F @Temperature 392 °F | DSC | |||
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft2-°F | ASTM E1530 | ||
| Melting Point | 340 °C | 644 °F | Peak; ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | Annealed; ASTM D648 | ||
| Glass Transition Temp, Tg | 150 °C | 302 °F | ASTM D3418 | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL 94 | ||
| V-0 @Thickness 20.3 mm | V-0 @Thickness 0.799 in | UL 94 | |||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 365 °C | 689 °F | |||
| Middle Barrel Temperature | 370 °C | 698 °F | |||
| Front Barrel Temperature | 375 °C | 707 °F | |||
| Nozzle Temperature | 380 °C | 716 °F | |||
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Agency Ratings | ISO 10993 | ||||
| ISO 10993-Part 1 | |||||
| Appearance | Beige | ||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Autoclave Sterilizable | ||||
| E-beam Sterilizable | |||||
| Ethylene Oxide Sterilizable | |||||
| Fatigue Resistant | |||||
| Flame Retardant | |||||
| Good Chemical Resistance | |||||
| Good Dimensional Stability | |||||
| Good Sterilizability | |||||
| Heat Sterilizable | |||||
| High Heat Resistance | |||||
| High Stiffness | |||||
| High Strength | |||||
| Radiation (Gamma) Resistant | |||||
| Radiation Sterilizable | |||||
| Radiotranslucent | |||||
| Steam Resistant | |||||
| Steam Sterilizable | |||||
| Forms | Pellets | ||||
| Powder | |||||
| Generic | PEEK | ||||
| Injection Rate | Fast | ||||
| Processing Method | Injection Molding | ||||
| Machining | |||||
| Profile Extrusion | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | ||||
| Uses | Aircraft Applications | ||||
| Connectors | |||||
| Dental Applications | |||||
| Electrical/Electronic Applications | |||||
| Film | |||||
| Hospital Goods | |||||
| Industrial Applications | |||||
| Medical Appliances | |||||
| Medical/Healthcare Applications | |||||
| Oil/Gas Applications | |||||
| Seals | |||||
| Surgical Instruments | |||||