- 熔體流動速率 [g/10min]: 36.0
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.53
- 拉伸強度 [MPa]: 102.0
- 彎曲模量 [MPa]: 3.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 | ||
| Viscosity | 150000 cP @Shear Rate 1000 1/s, Temperature 400 °C | 150000 cP @Shear Rate 1000 1/s, Temperature 752 °F | Melt; ASTM D3835 | ||
| Linear Mold Shrinkage, Flow | 0.014 - 0.016 cm/cm @Thickness 0.318 mm | 0.014 - 0.016 in/in @Thickness 0.0125 in | 5" x 0.5" x 0.125"; ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.015 - 0.017 cm/cm @Thickness 3.18 mm | 0.015 - 0.017 in/in @Thickness 0.125 in | 5" x 0.5" x 0.125"; ASTM D955 | ||
| Melt Flow | 36 g/10 min @Load 2.16 kg, Temperature 400 °C | 36 g/10 min @Load 4.76 lb, Temperature 752 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 102 | 102 | M-Scale; ASTM D785 | ||
| Tensile Strength | 100 MPa | 14500 psi | 51 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 102 MPa | 14800 psi | ISO 527-2/1A/50 | ||
| Elongation at Break | 10 - 20 % | 10 - 20 % | 50 mm/min; ASTM D638 | ||
| 10 - 20 % | 10 - 20 % | ISO 527-2/1A/50 | |||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-2/1A/50 | ||
| 5.2 % | 5.2 % | 50 mm/min; ASTM D638 | |||
| Tensile Modulus | 3.70 GPa | 537 ksi | 1.0 mm/min; ASTM D638 | ||
| 4.00 GPa | 580 ksi | ISO 527-2/1A/1 | |||
| Flexural Strength | 134 MPa | 19400 psi | ISO 178 | ||
| 153 MPa | 22200 psi | ASTM D790 | |||
| Flexural Modulus | 3.80 GPa | 551 ksi | ASTM D790 | ||
| 3.90 GPa | 566 ksi | ISO 178 | |||
| Compressive Strength | 123 MPa | 17800 psi | ASTM D695 | ||
| Poissons Ratio | 0.37 | 0.37 | ASTM E132 | ||
| Shear Modulus | 1.35 - 1.46 GPa | 196 - 212 ksi | Calculated | ||
| Shear Strength | 95.1 MPa | 13800 psi | ASTM D732 | ||
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 | ||
| NB | NB | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 4.90 kJ/m2 | 2.33 ft-lb/in2 | ISO 180 | ||
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.80e+17 ohm-cm | 3.80e+17 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 | ||
| Dielectric Constant | 3.01 @Frequency 1000 Hz | 3.01 @Frequency 1000 Hz | ASTM D150 | ||
| 3.07 @Frequency 1.00e+6 Hz | 3.07 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| 3.1 @Frequency 60.0 Hz | 3.1 @Frequency 60.0 Hz | ASTM D150 | |||
| Dielectric Strength | 0.591 kV/mm @Thickness 3.00 mm | 15.0 kV/in @Thickness 0.118 in | ASTM D149 | ||
| Dissipation Factor | 0.0010 @Frequency 1000 Hz | 0.0010 @Frequency 1000 Hz | ASTM D150 | ||
| 0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | ASTM D150 | |||
| 0.0030 @Frequency 1.00e+6 Hz | 0.0030 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 μm/m-°C @Temperature -50.0 - 50.0 °C | 27.8 μin/in-°F @Temperature -58.0 - 122 °F | TMA; ASTM E831 | ||
| Specific Heat Capacity | 1.33 J/g-°C @Temperature 50.0 °C | 0.318 BTU/lb-°F @Temperature 122 °F | DSC | ||
| 1.93 J/g-°C @Temperature 200 °C | 0.461 BTU/lb-°F @Temperature 392 °F | DSC | |||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft2-°F | ASTM E1530 | ||
| Melting Point | 343 °C | 649 °F | Peak; ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Annealed; ASTM D648 | ||
| Glass Transition Temp, Tg | 147 °C | 297 °F | ASTM D3418 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 355 °C | 671 °F | |||
| Middle Barrel Temperature | 365 °C | 689 °F | |||
| Front Barrel Temperature | 370 °C | 698 °F | |||
| Nozzle Temperature | 375 °C | 707 °F | |||
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Agency Ratings | ISO 10993 | ||||
| ISO 10993-Part 1 | |||||
| Appearance | Black | ||||
| Natural Color | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Autoclave Sterilizable | ||||
| Biocompatible | |||||
| Ductile | |||||
| E-beam Sterilizable | |||||
| Ethylene Oxide Sterilizable | |||||
| Fatigue Resistant | |||||
| Flame Retardant | |||||
| Good Chemical Resistance | |||||
| Good Dimensional Stability | |||||
| Good Impact Resistance | |||||
| Good Sterilizability | |||||
| Heat Sterilizable | |||||
| High Flow | |||||
| High Heat Resistance | |||||
| Radiation (Gamma) Resistant | |||||
| Radiation Sterilizable | |||||
| Radiotranslucent | |||||
| Steam Resistant | |||||
| Steam Sterilizable | |||||
| Forms | Pellets | ||||
| Generic | PEEK | ||||
| Injection Rate | Fast | ||||
| Processing Method | Extrusion Blow Molding | ||||
| Fiber (Spinning) Extrusion | |||||
| Film Extrusion | |||||
| Injection Molding | |||||
| Machining | |||||
| Profile Extrusion | |||||
| Thermoforming | |||||
| Wire & Cable Extrusion | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | ||||
| Uses | Aircraft Applications | ||||
| Connectors | |||||
| Dental Applications | |||||
| Electrical/Electronic Applications | |||||
| Film | |||||
| Hospital Goods | |||||
| Industrial Applications | |||||
| Medical Appliances | |||||
| Medical/Healthcare Applications | |||||
| Oil/Gas Applications | |||||
| Pump Parts | |||||
| Seals | |||||
| Surgical Instruments | |||||