- 熔體流動(dòng)速率 [g/10min]: 3.0
- 吸水率 [%]: 0.1
- 缺口沖擊強(qiáng)度: 0.91
- 拉伸強(qiáng)度 [MPa]: 96.0
- 彎曲模量 [MPa]: 3.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ASTM D955 | ||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 400 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 752 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 88 @Time 1.00 sec | 88 @Time 0.000278 hour | ASTM D2240 | ||
| Tensile Strength | 95.0 MPa | 13800 psi | 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | ISO 527-2/1A/50 | ||
| Elongation at Break | 20 - 30 % | 20 - 30 % | 50 mm/min; ASTM D638 | ||
| 20 - 30 % | 20 - 30 % | ISO 527-2/1A/50 | |||
| Elongation at Yield | 4.9 % | 4.9 % | ISO 527-2/1A/50 | ||
| 5.2 % | 5.2 % | 50 mm/min; ASTM D638 | |||
| Tensile Modulus | 3.50 GPa | 508 ksi | 50 mm/min; ASTM D638 | ||
| 3.83 GPa | 555 ksi | ISO 527-2/1A/1 | |||
| Flexural Strength | 146 MPa | 21200 psi | ASTM D790 | ||
| Flexural Modulus | 3.70 GPa | 537 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 | ||
| NB | NB | ASTM D4812 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 43.0 μm/m-°C @Temperature -50.0 - 50.0 °C | 23.9 μin/in-°F @Temperature -58.0 - 122 °F | TMA; ASTM E831 | ||
| Melting Point | 340 °C | 644 °F | Peak; ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | Unannealed; ASTM D648 | ||
| Glass Transition Temp, Tg | 150 °C | 302 °F | ASTM D3418 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 355 °C | 671 °F | |||
| Middle Barrel Temperature | 365 °C | 689 °F | |||
| Front Barrel Temperature | 370 °C | 698 °F | |||
| Nozzle Temperature | 375 °C | 707 °F | |||
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Ductile | ||||
| Fatigue Resistant | |||||
| Flame Retardant | |||||
| Good Chemical Resistance | |||||
| Good Dimensional Stability | |||||
| Good Impact Resistance | |||||
| High Heat Resistance | |||||
| Forms | Pellets | non-lubricated | |||
| Generic | PEEK | ||||
| Injection Rate | Fast | ||||
| Processing Method | Injection Molding | ||||
| Machining | |||||
| Profile Extrusion | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | ||||
| Uses | Aircraft Applications | ||||
| Automotive Applications | |||||
| Electrical/Electronic Applications | |||||
| Film | |||||
| Industrial Applications | |||||
| Medical/Healthcare Applications | |||||
| Oil/Gas Applications | |||||