- 熔體流動速率 [g/10min]: 15.5
- 密度 [g/cm3]: 1.0
- 拉伸強度 [MPa]: 16.0
- 熱變形溫度 [℃]: 69.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in3 | |
| Melt Flow | 15.5 g/10 min @Load 2.16 kg, Temperature 235 °C | 15.5 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 16.0 MPa @Strain 50.0 % | 2320 psi @Strain 50.0 % | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 0.180 GPa | 26.1 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 6.00e+10 ohm-cm | 6.00e+10 ohm-cm | |
| Surface Resistance | 4.00e+13 ohm | 4.00e+13 ohm | |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 90.0 μm/m-°C @Temperature 20.0 °C | 50.0 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 150 °C | 302 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 °C | 106 °F | |
| Vicat Softening Point | 180 °C | 356 °F | 50°C/hr; 50N |
| Flammability, UL94 | V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |