- 密度 [g/cm3]: 1.1
- 缺口沖擊強度: 0.534
- 斷裂伸長率 [%]: 82.7
- 彎曲強度 [MPa]: 58.6
- 彎曲模量 [MPa]: 2.41
- 硬度: 108.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 - 1.42 g/cc | 0.0397 - 0.0513 lb/in3 | Average value: 1.26 g/cc Grade Count:4 |
| Linear Mold Shrinkage | 0.00400 - 0.00600 cm/cm | 0.00400 - 0.00600 in/in | Average value: 0.00500 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 | 108 | Average value: 108 Grade Count:3 |
| Tensile Strength, Ultimate | 58.6 - 82.7 MPa | 8500 - 12000 psi | Average value: 66.4 MPa Grade Count:4 |
| Elongation at Break | 2.00 - 17.3 % | 2.00 - 17.3 % | Average value: 8.22 % Grade Count:6 |
| Modulus of Elasticity | 2.76 - 4.14 GPa | 400 - 600 ksi | Average value: 3.22 GPa Grade Count:6 |
| Flexural Yield Strength | 82.7 - 100 MPa | 12000 - 14500 psi | Average value: 92.2 MPa Grade Count:4 |
| Flexural Modulus | 2.41 - 3.45 GPa | 350 - 500 ksi | Average value: 3.02 GPa Grade Count:4 |
| Izod Impact, Notched | 0.534 - 0.747 J/cm | 1.00 - 1.40 ft-lb/in | Average value: 0.614 J/cm Grade Count:4 |
| Izod Impact, Unnotched | 3.74 - 5.87 J/cm | 7.00 - 11.0 ft-lb/in | Average value: 4.81 J/cm Grade Count:4 |
| Charpy Impact Unnotched | 9.17 - 10.0 J/cm2 @Temperature -30.0 - -30.0 °C | 43.6 - 47.6 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 9.59 J/cm2 Grade Count:2 |
| Charpy Impact, Notched | 0.440 - 0.550 J/cm2 @Temperature -30.0 - -30.0 °C | 2.09 - 2.62 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.495 J/cm2 Grade Count:2 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 37.8 - 65.6 °C | 100 - 150 °F | Average value: 51.7 °C Grade Count:4 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:4 |