- 熔體流動(dòng)速率 [g/10min]: 0.8
- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 1.9
- 拉伸強(qiáng)度 [MPa]: 41.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in3 | |
| Water Absorption | 1.9 % | 1.9 % | |
| Melt Flow | 0.80 g/10 min @Load 10.0 kg, Temperature 235 °C | 0.80 g/10 min @Load 22.0 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 1.36 GPa | 197 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | Low Temp |
| NB | NB | ||
| Charpy Impact, Notched | 1.10 J/cm2 @Temperature -30.0 °C | 5.24 ft-lb/in2 @Temperature -22.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 183 °C | 361 °F | 10°C/min |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||