- 吸水率 [%]: 3.1
- 缺口沖擊強度: 3.52
- 彎曲強度 [MPa]: 49.0
- 彎曲模量 [MPa]: 1.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 3.1 % | 3.1 % | 24 hrs; DIN 53714 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 74 | 74 | |
| Tensile Strength, Ultimate | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 250 % | 250 % | ASTM D638 |
| Tensile Modulus | 1.20 GPa | 174 ksi | ASTM D638 |
| Flexural Modulus | 1.17 GPa | 170 ksi | ASTM D790 |
| Izod Impact, Notched | 3.52 J/cm | 6.59 ft-lb/in | Method B; Ductile Failure |
| 0.430 J/cm @Temperature -40.0 °C | 0.806 ft-lb/in @Temperature -40.0 °F | Method B; Brittle Failure | |
| Charpy Impact, Notched | 1.20 J/cm2 | 5.71 ft-lb/in2 | Brittle Failure; ASTM D256B |
| 0.310 J/cm2 @Temperature -40.0 °C | 1.48 ft-lb/in2 @Temperature -40.0 °F | Method B; Brittle Failure | |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.1 @Frequency 100000 Hz | 4.1 @Frequency 100000 Hz | |
| 7.9 @Frequency 1000 Hz | 7.9 @Frequency 1000 Hz | ||
| 15.3 @Frequency 50 Hz | 15.3 @Frequency 50 Hz | ||
| Dielectric Strength | 13.0 kV/mm | 330 kV/in | |
| Dissipation Factor | 0.10 @Frequency 100000 Hz | 0.10 @Frequency 100000 Hz | ASTM D150 |
| 0.30 @Frequency 1000 Hz | 0.30 @Frequency 1000 Hz | ASTM D150 | |
| Comparative Tracking Index | 400 V | 400 V | ASTM D257 |