- 缺口沖擊強度: 2670.0
- 彎曲模量 [MPa]: 6.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 4.00 g/cc | 4.00 g/cc | Internal Method |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 25.0 MPa | 3630 psi | ISO 527 |
| Elongation at Break | 0.50 % | 0.50 % | ISO 527 |
| Tensile Modulus | 7.50 GPa | 1090 ksi | ISO 527 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ISO 178 |
| Izod Impact, Notched | 2670 J/cm | 5000 ft-lb/in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | target |