- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 1.8
- 缺口沖擊強度: 12.0
- 彎曲模量 [MPa]: 5.70
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 30 % | 30 % | DAM | ||
| Water Absorption | 1.8 % @Temperature 23.0 °C | 1.8 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 6.2 % @Temperature 23.0 °C | 6.2 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C | 16000 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 170 MPa @Temperature 23.0 °C | 24700 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 5.70 GPa @Temperature 23.0 °C | 827 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 9.10 GPa @Temperature 23.0 °C | 1320 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 5.70 GPa @Temperature 23.0 °C | 827 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 9.00 GPa @Temperature 23.0 °C | 1310 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Shear Modulus | 0.00100 GPa @Temperature 228 °C | 0.145 ksi @Temperature 442 °F | DAM; ISO 6721 | ||
| 0.0460 GPa @Temperature 224 °C | 6.67 ksi @Temperature 435 °F | DAM; ISO 6721 | |||
| 0.122 GPa @Temperature 220 °C | 17.7 ksi @Temperature 428 °F | DAM; ISO 6721 | |||
| 0.199 GPa @Temperature 216 °C | 28.9 ksi @Temperature 421 °F | DAM; ISO 6721 | |||
| 0.232 GPa @Temperature 214 °C | 33.6 ksi @Temperature 417 °F | DAM; ISO 6721 | |||
| 0.290 GPa @Temperature 210 °C | 42.1 ksi @Temperature 410 °F | DAM; ISO 6721 | |||
| 0.347 GPa @Temperature 204 °C | 50.3 ksi @Temperature 399 °F | DAM; ISO 6721 | |||
| 0.383 GPa @Temperature 200 °C | 55.6 ksi @Temperature 392 °F | DAM; ISO 6721 | |||
| 0.445 GPa @Temperature 190 °C | 64.5 ksi @Temperature 374 °F | DAM; ISO 6721 | |||
| 0.482 GPa @Temperature 180 °C | 69.9 ksi @Temperature 356 °F | DAM; ISO 6721 | |||
| 0.506 GPa @Temperature 170 °C | 73.4 ksi @Temperature 338 °F | DAM; ISO 6721 | |||
| 0.524 GPa @Temperature 160 °C | 76.0 ksi @Temperature 320 °F | DAM; ISO 6721 | |||
| 0.537 GPa @Temperature 150 °C | 77.9 ksi @Temperature 302 °F | DAM; ISO 6721 | |||
| 0.548 GPa @Temperature 140 °C | 79.5 ksi @Temperature 284 °F | DAM; ISO 6721 | |||
| 0.557 GPa @Temperature 130 °C | 80.8 ksi @Temperature 266 °F | DAM; ISO 6721 | |||
| 0.569 GPa @Temperature 118 °C | 82.5 ksi @Temperature 244 °F | DAM; ISO 6721 | |||
| 0.578 GPa @Temperature 110 °C | 83.8 ksi @Temperature 230 °F | DAM; ISO 6721 | |||
| 0.593 GPa @Temperature 100 °C | 86.0 ksi @Temperature 212 °F | DAM; ISO 6721 | |||
| 0.614 GPa @Temperature 90.0 °C | 89.1 ksi @Temperature 194 °F | DAM; ISO 6721 | |||
| 0.650 GPa @Temperature 80.0 °C | 94.3 ksi @Temperature 176 °F | DAM; ISO 6721 | |||
| 0.712 GPa @Temperature 70.0 °C | 103 ksi @Temperature 158 °F | DAM; ISO 6721 | |||
| 0.834 GPa @Temperature 60.0 °C | 121 ksi @Temperature 140 °F | DAM; ISO 6721 | |||
| 1.111 GPa @Temperature 50.0 °C | 161.1 ksi @Temperature 122 °F | DAM; ISO 6721 | |||
| 1.443 GPa @Temperature 40.0 °C | 209.3 ksi @Temperature 104 °F | DAM; ISO 6721 | |||
| 1.573 GPa @Temperature 30.0 °C | 228.1 ksi @Temperature 86.0 °F | DAM; ISO 6721 | |||
| 1.656 GPa @Temperature 20.0 °C | 240.2 ksi @Temperature 68.0 °F | DAM; ISO 6721 | |||
| 1.716 GPa @Temperature 10.0 °C | 248.9 ksi @Temperature 50.0 °F | DAM; ISO 6721 | |||
| 1.751 GPa @Temperature 0.000 °C | 254.0 ksi @Temperature 32.0 °F | DAM; ISO 6721 | |||
| 1.769 GPa @Temperature -10.0 °C | 256.6 ksi @Temperature 14.0 °F | DAM; ISO 6721 | |||
| 1.783 GPa @Temperature -20.0 °C | 258.6 ksi @Temperature -4.00 °F | DAM; ISO 6721 | |||
| 1.805 GPa @Temperature -30.0 °C | 261.8 ksi @Temperature -22.0 °F | DAM; ISO 6721 | |||
| 1.847 GPa @Temperature -40.0 °C | 267.9 ksi @Temperature -40.0 °F | DAM; ISO 6721 | |||
| 1.93 GPa @Temperature -50.0 °C | 280 ksi @Temperature -58.0 °F | DAM; ISO 6721 | |||
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 180/1A | ||
| 12.0 kJ/m2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 180/1A | |||
| 17.0 kJ/m2 @Temperature 23.0 °C | 8.09 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 24.0 kJ/m2 @Temperature 23.0 °C | 11.4 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1U | ||
| 80.0 kJ/m2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1U | |||
| Charpy Impact Unnotched | 9.40 J/cm2 @Temperature -30.0 °C | 44.7 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| 10.0 J/cm2 @Temperature -30.0 °C | 47.6 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| 10.0 J/cm2 @Temperature 23.0 °C | 47.6 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 10.0 J/cm2 @Temperature 23.0 °C | 47.6 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.30 J/cm2 @Temperature -30.0 °C | 6.19 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 2.00 J/cm2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 2.50 J/cm2 @Temperature 23.0 °C | 11.9 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 120 μm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 120 μm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 270 °C | 518 °F | DAM; Optimum | |||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | DAM | ||
| 80.0 °C | 176 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Chemical Resistance, Good | DAM | ||||
| Fatigue Resistant | DAM | ||||
| Fatigue Resistant | DAM | ||||
| Fuel Resistant | DAM | ||||
| Fuel Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Impact Modified | DAM | ||||
| Impact Modified | DAM | ||||
| Impact Resistance, Good | DAM | ||||
| Impact Resistance, Good | DAM | ||||
| Oil Resistant | DAM | ||||
| Oil Resistant | DAM | ||||
| Toughness, Good | DAM | ||||
| Toughness, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA6-IGF30< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA6 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA6-IGF30 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||