- 缺口沖擊強度: 4000.0
- 彎曲模量 [MPa]: 2.80
- 熱變形溫度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.50 g/cc | 2.50 g/cc | Internal Method |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 31.0 MPa | 4500 psi | ISO 527 |
| Elongation at Break | 10 % | 10 % | ISO 527 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Izod Impact, Notched | 4000 J/cm | 7500 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | target |