- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 2.0
- 彎曲模量 [MPa]: 10.1
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 35 % | 35 % | DAM | ||
| Water Absorption | 2.0 % @Temperature 23.0 °C | 2.0 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa @Temperature 23.0 °C | 17400 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 197 MPa @Temperature 23.0 °C | 28600 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Stress | 0.510 MPa @Strain 0.000 %, Temperature 200 °C | 74.0 psi @Strain 0.000 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | ||
| 0.830 MPa @Strain 0.000 %, Temperature 180 °C | 120 psi @Strain 0.000 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 0.880 MPa @Strain 0.000 %, Temperature 150 °C | 128 psi @Strain 0.000 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.910 MPa @Strain 0.000 %, Temperature 150 °C | 132 psi @Strain 0.000 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 0.950 MPa @Strain 0.000 %, Temperature 120 °C | 138 psi @Strain 0.000 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.09 MPa @Strain 0.000 %, Temperature 120 °C | 158 psi @Strain 0.000 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 1.09 MPa @Strain 0.000 %, Temperature 90.0 °C | 158 psi @Strain 0.000 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.17 MPa @Strain 0.000 %, Temperature 90.0 °C | 170 psi @Strain 0.000 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 1.19 MPa @Strain 0.000 %, Temperature 60.0 °C | 173 psi @Strain 0.000 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.23 MPa @Strain 0.000 %, Temperature 40.0 °C | 178 psi @Strain 0.000 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.28 MPa @Strain 0.000 %, Temperature 23.0 °C | 186 psi @Strain 0.000 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.34 MPa @Strain 0.000 %, Temperature 0.000 °C | 194 psi @Strain 0.000 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.38 MPa @Strain 0.000 %, Temperature 60.0 °C | 200 psi @Strain 0.000 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 1.56 MPa @Strain 0.000 %, Temperature 0.000 °C | 226 psi @Strain 0.000 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 1.81 MPa @Strain 0.000 %, Temperature 40.0 °C | 263 psi @Strain 0.000 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 1.92 MPa @Strain 0.000 %, Temperature -20.0 °C | 278 psi @Strain 0.000 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.95 MPa @Strain 0.000 %, Temperature -20.0 °C | 283 psi @Strain 0.000 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 1.98 MPa @Strain 0.000 %, Temperature 23.0 °C | 287 psi @Strain 0.000 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 2.76 MPa @Strain 0.0400 %, Temperature -20.0 °C | 400 psi @Strain 0.0400 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.90 MPa @Strain 0.100 %, Temperature 200 °C | 421 psi @Strain 0.100 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 2.94 MPa @Strain 0.0600 %, Temperature 150 °C | 426 psi @Strain 0.0600 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.19 MPa @Strain 0.0600 %, Temperature 180 °C | 463 psi @Strain 0.0600 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 3.32 MPa @Strain 0.0600 %, Temperature 120 °C | 482 psi @Strain 0.0600 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.75 MPa @Strain 0.0200 %, Temperature -20.0 °C | 544 psi @Strain 0.0200 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 3.90 MPa @Strain 0.0700 %, Temperature 150 °C | 566 psi @Strain 0.0700 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 3.92 MPa @Strain 0.0500 %, Temperature 90.0 °C | 569 psi @Strain 0.0500 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.40 MPa @Strain 0.0600 %, Temperature 60.0 °C | 638 psi @Strain 0.0600 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.42 MPa @Strain 0.0700 %, Temperature 120 °C | 641 psi @Strain 0.0700 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 4.70 MPa @Strain 0.0600 %, Temperature 40.0 °C | 682 psi @Strain 0.0600 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.86 MPa @Strain 0.0800 %, Temperature 90.0 °C | 705 psi @Strain 0.0800 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 4.88 MPa @Strain 0.190 %, Temperature 200 °C | 708 psi @Strain 0.190 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 4.95 MPa @Strain 0.110 %, Temperature 150 °C | 718 psi @Strain 0.110 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.23 MPa @Strain 0.0500 %, Temperature 23.0 °C | 759 psi @Strain 0.0500 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.52 MPa @Strain 0.0700 %, Temperature 60.0 °C | 801 psi @Strain 0.0700 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 5.54 MPa @Strain 0.140 %, Temperature 180 °C | 804 psi @Strain 0.140 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 5.69 MPa @Strain 0.0500 %, Temperature 0.000 °C | 825 psi @Strain 0.0500 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.70 MPa @Strain 0.120 %, Temperature 120 °C | 827 psi @Strain 0.120 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.99 MPa @Strain 0.0500 %, Temperature 40.0 °C | 869 psi @Strain 0.0500 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 6.51 MPa @Strain 0.0400 %, Temperature 23.0 °C | 944 psi @Strain 0.0400 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 6.60 MPa @Strain 0.120 %, Temperature 90.0 °C | 957 psi @Strain 0.120 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 6.76 MPa @Strain 0.0500 %, Temperature 0.000 °C | 980 psi @Strain 0.0500 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 6.90 MPa @Strain 0.170 %, Temperature 150 °C | 1000 psi @Strain 0.170 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 6.94 MPa @Strain 0.150 %, Temperature 150 °C | 1010 psi @Strain 0.150 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 7.54 MPa @Strain 0.0900 %, Temperature -20.0 °C | 1090 psi @Strain 0.0900 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.63 MPa @Strain 0.110 %, Temperature 60.0 °C | 1110 psi @Strain 0.110 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.69 MPa @Strain 0.200 %, Temperature 180 °C | 1120 psi @Strain 0.200 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 7.75 MPa @Strain 0.150 %, Temperature 120 °C | 1120 psi @Strain 0.150 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 7.91 MPa @Strain 0.180 %, Temperature 120 °C | 1150 psi @Strain 0.180 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.13 MPa @Strain 0.110 %, Temperature 40.0 °C | 1180 psi @Strain 0.110 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.56 MPa @Strain 0.150 %, Temperature 90.0 °C | 1240 psi @Strain 0.150 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 8.71 MPa @Strain 0.230 %, Temperature 150 °C | 1260 psi @Strain 0.230 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.96 MPa @Strain 0.110 %, Temperature 23.0 °C | 1300 psi @Strain 0.110 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.16 MPa @Strain 0.180 %, Temperature 90.0 °C | 1330 psi @Strain 0.180 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.23 MPa @Strain 0.440 %, Temperature 200 °C | 1340 psi @Strain 0.440 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 9.51 MPa @Strain 0.130 %, Temperature 60.0 °C | 1380 psi @Strain 0.130 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 9.64 MPa @Strain 0.220 %, Temperature 150 °C | 1400 psi @Strain 0.220 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 9.77 MPa @Strain 0.0600 %, Temperature -20.0 °C | 1420 psi @Strain 0.0600 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 10.05 MPa @Strain 0.230 %, Temperature 120 °C | 1458 psi @Strain 0.230 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.15 MPa @Strain 0.0900 %, Temperature 0.000 °C | 1472 psi @Strain 0.0900 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.4 MPa @Strain 0.100 %, Temperature 40.0 °C | 1510 psi @Strain 0.100 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 10.69 MPa @Strain 0.180 %, Temperature 60.0 °C | 1550 psi @Strain 0.180 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.89 MPa @Strain 0.220 %, Temperature 120 °C | 1579 psi @Strain 0.220 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 10.96 MPa @Strain 0.0800 %, Temperature 23.0 °C | 1590 psi @Strain 0.0800 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 11.55 MPa @Strain 0.170 %, Temperature 40.0 °C | 1675 psi @Strain 0.170 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.56 MPa @Strain 0.230 %, Temperature 90.0 °C | 1677 psi @Strain 0.230 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.95 MPa @Strain 0.220 %, Temperature 90.0 °C | 1733 psi @Strain 0.220 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 12.06 MPa @Strain 0.100 %, Temperature 0.000 °C | 1749 psi @Strain 0.100 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 12.2 MPa @Strain 0.340 %, Temperature 180 °C | 1770 psi @Strain 0.340 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 12.53 MPa @Strain 0.130 %, Temperature -20.0 °C | 1817 psi @Strain 0.130 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.59 MPa @Strain 0.160 %, Temperature 23.0 °C | 1826 psi @Strain 0.160 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.46 MPa @Strain 0.190 %, Temperature 60.0 °C | 1952 psi @Strain 0.190 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 13.57 MPa @Strain 0.240 %, Temperature 60.0 °C | 1968 psi @Strain 0.240 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.39 MPa @Strain 0.410 %, Temperature 150 °C | 2087 psi @Strain 0.410 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.42 MPa @Strain 0.130 %, Temperature 0.000 °C | 2091 psi @Strain 0.130 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.68 MPa @Strain 0.230 %, Temperature 40.0 °C | 2129 psi @Strain 0.230 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.72 MPa @Strain 0.980 %, Temperature 200 °C | 2135 psi @Strain 0.980 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 14.74 MPa @Strain 0.140 %, Temperature 40.0 °C | 2138 psi @Strain 0.140 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 15.53 MPa @Strain 0.100 %, Temperature -20.0 °C | 2252 psi @Strain 0.100 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 15.71 MPa @Strain 0.120 %, Temperature 23.0 °C | 2279 psi @Strain 0.120 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 16.28 MPa @Strain 0.220 %, Temperature 23.0 °C | 2361 psi @Strain 0.220 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.97 MPa @Strain 0.140 %, Temperature 0.000 °C | 2461 psi @Strain 0.140 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 17.36 MPa @Strain 0.170 %, Temperature -20.0 °C | 2518 psi @Strain 0.170 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 17.46 MPa @Strain 0.250 %, Temperature 60.0 °C | 2532 psi @Strain 0.250 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 17.71 MPa @Strain 0.420 %, Temperature 150 °C | 2569 psi @Strain 0.420 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 18.14 MPa @Strain 0.480 %, Temperature 120 °C | 2631 psi @Strain 0.480 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.41 MPa @Strain 1.50 %, Temperature 200 °C | 2670 psi @Strain 1.50 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 18.44 MPa @Strain 0.180 %, Temperature 0.000 °C | 2675 psi @Strain 0.180 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.0 MPa @Strain 0.190 %, Temperature 40.0 °C | 2760 psi @Strain 0.190 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 19.88 MPa @Strain 0.430 %, Temperature 120 °C | 2883 psi @Strain 0.430 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 20.26 MPa @Strain 0.690 %, Temperature 180 °C | 2938 psi @Strain 0.690 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 20.28 MPa @Strain 0.170 %, Temperature 23.0 °C | 2941 psi @Strain 0.170 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 20.51 MPa @Strain 0.460 %, Temperature 90.0 °C | 2975 psi @Strain 0.460 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.27 MPa @Strain 2.04 %, Temperature 200 °C | 3085 psi @Strain 2.04 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 21.34 MPa @Strain 0.690 %, Temperature 150 °C | 3095 psi @Strain 0.690 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.44 MPa @Strain 0.150 %, Temperature -20.0 °C | 3110 psi @Strain 0.150 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 21.97 MPa @Strain 0.180 %, Temperature 0.000 °C | 3186 psi @Strain 0.180 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 21.97 MPa @Strain 0.210 %, Temperature -20.0 °C | 3186 psi @Strain 0.210 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.53 MPa @Strain 0.220 %, Temperature 0.000 °C | 3268 psi @Strain 0.220 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.05 MPa @Strain 0.430 %, Temperature 60.0 °C | 3343 psi @Strain 0.430 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.12 MPa @Strain 0.460 %, Temperature 90.0 °C | 3353 psi @Strain 0.460 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 23.13 MPa @Strain 0.240 %, Temperature 40.0 °C | 3355 psi @Strain 0.240 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 23.56 MPa @Strain 2.61 %, Temperature 200 °C | 3417 psi @Strain 2.61 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 24.72 MPa @Strain 0.210 %, Temperature 23.0 °C | 3585 psi @Strain 0.210 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 25.51 MPa @Strain 0.430 %, Temperature 40.0 °C | 3700 psi @Strain 0.430 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.57 MPa @Strain 3.12 %, Temperature 200 °C | 3709 psi @Strain 3.12 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 25.96 MPa @Strain 1.06 %, Temperature 180 °C | 3765 psi @Strain 1.06 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 26.05 MPa @Strain 0.780 %, Temperature 120 °C | 3778 psi @Strain 0.780 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.38 MPa @Strain 0.380 %, Temperature 23.0 °C | 3826 psi @Strain 0.380 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.72 MPa @Strain 0.980 %, Temperature 150 °C | 3875 psi @Strain 0.980 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.77 MPa @Strain 0.230 %, Temperature 0.000 °C | 3883 psi @Strain 0.230 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 27.11 MPa @Strain 0.250 %, Temperature -20.0 °C | 3932 psi @Strain 0.250 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.11 MPa @Strain 0.190 %, Temperature -20.0 °C | 3932 psi @Strain 0.190 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 27.32 MPa @Strain 3.70 %, Temperature 200 °C | 3962 psi @Strain 3.70 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 27.87 MPa @Strain 0.750 %, Temperature 150 °C | 4042 psi @Strain 0.750 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 28.91 MPa @Strain 4.20 %, Temperature 200 °C | 4193 psi @Strain 4.20 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 29.3 MPa @Strain 0.240 %, Temperature 23.0 °C | 4250 psi @Strain 0.240 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 29.73 MPa @Strain 0.760 %, Temperature 90.0 °C | 4312 psi @Strain 0.760 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 30.38 MPa @Strain 1.43 %, Temperature 180 °C | 4406 psi @Strain 1.43 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 30.43 MPa @Strain 4.75 %, Temperature 200 °C | 4414 psi @Strain 4.75 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 31.05 MPa @Strain 1.30 %, Temperature 150 °C | 4503 psi @Strain 1.30 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 31.8 MPa @Strain 5.33 %, Temperature 200 °C | 4610 psi @Strain 5.33 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 31.88 MPa @Strain 0.770 %, Temperature 120 °C | 4624 psi @Strain 0.770 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 32.49 MPa @Strain 1.10 %, Temperature 120 °C | 4712 psi @Strain 1.10 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 32.82 MPa @Strain 0.230 %, Temperature -20.0 °C | 4760 psi @Strain 0.230 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 33.03 MPa @Strain 5.84 %, Temperature 200 °C | 4791 psi @Strain 5.84 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 33.19 MPa @Strain 0.680 %, Temperature 60.0 °C | 4814 psi @Strain 0.680 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.64 MPa @Strain 0.330 %, Temperature 0.000 °C | 4879 psi @Strain 0.330 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 34.03 MPa @Strain 1.82 %, Temperature 180 °C | 4936 psi @Strain 1.82 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 34.31 MPa @Strain 6.45 %, Temperature 200 °C | 4976 psi @Strain 6.45 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 34.68 MPa @Strain 1.61 %, Temperature 150 °C | 5030 psi @Strain 1.61 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.2 MPa @Strain 0.760 %, Temperature 90.0 °C | 5110 psi @Strain 0.760 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 35.28 MPa @Strain 0.650 %, Temperature 40.0 °C | 5117 psi @Strain 0.650 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.45 MPa @Strain 6.97 %, Temperature 200 °C | 5142 psi @Strain 6.97 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 35.53 MPa @Strain 0.370 %, Temperature 40.0 °C | 5153 psi @Strain 0.370 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 35.74 MPa @Strain 1.10 %, Temperature 150 °C | 5184 psi @Strain 1.10 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 36.01 MPa @Strain 0.560 %, Temperature 60.0 °C | 5223 psi @Strain 0.560 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 36.68 MPa @Strain 7.42 %, Temperature 200 °C | 5320 psi @Strain 7.42 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 37.01 MPa @Strain 2.21 %, Temperature 180 °C | 5368 psi @Strain 2.21 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 37.14 MPa @Strain 1.06 %, Temperature 90.0 °C | 5387 psi @Strain 1.06 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.31 MPa @Strain 0.580 %, Temperature 23.0 °C | 5411 psi @Strain 0.580 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.75 MPa @Strain 1.42 %, Temperature 120 °C | 5475 psi @Strain 1.42 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.8 MPa @Strain 7.96 %, Temperature 200 °C | 5480 psi @Strain 7.96 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 37.88 MPa @Strain 1.93 %, Temperature 150 °C | 5494 psi @Strain 1.93 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 38.55 MPa @Strain 0.330 %, Temperature 0.000 °C | 5591 psi @Strain 0.330 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 38.9 MPa @Strain 8.60 %, Temperature 200 °C | 5640 psi @Strain 8.60 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 39.58 MPa @Strain 2.60 %, Temperature 180 °C | 5741 psi @Strain 2.60 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 39.9 MPa @Strain 9.21 %, Temperature 200 °C | 5790 psi @Strain 9.21 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 40.58 MPa @Strain 1.09 %, Temperature 120 °C | 5886 psi @Strain 1.09 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 40.63 MPa @Strain 2.26 %, Temperature 150 °C | 5893 psi @Strain 2.26 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 40.88 MPa @Strain 9.68 %, Temperature 200 °C | 5929 psi @Strain 9.68 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 40.97 MPa @Strain 0.910 %, Temperature 60.0 °C | 5942 psi @Strain 0.910 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 41.33 MPa @Strain 1.43 %, Temperature 150 °C | 5994 psi @Strain 1.43 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 41.82 MPa @Strain 2.98 %, Temperature 180 °C | 6065 psi @Strain 2.98 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 41.84 MPa @Strain 10.14 %, Temperature 200 °C | 6068 psi @Strain 10.14 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 42.09 MPa @Strain 1.73 %, Temperature 120 °C | 6105 psi @Strain 1.73 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 42.67 MPa @Strain 10.78 %, Temperature 200 °C | 6189 psi @Strain 10.78 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 42.83 MPa @Strain 0.850 %, Temperature 40.0 °C | 6212 psi @Strain 0.850 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.01 MPa @Strain 1.35 %, Temperature 90.0 °C | 6238 psi @Strain 1.35 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.05 MPa @Strain 2.59 %, Temperature 150 °C | 6244 psi @Strain 2.59 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.21 MPa @Strain 12.23 %, Temperature 200 °C | 6267 psi @Strain 12.23 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 43.3 MPa @Strain 11.45 %, Temperature 200 °C | 6280 psi @Strain 11.45 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 43.85 MPa @Strain 3.37 %, Temperature 180 °C | 6360 psi @Strain 3.37 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 45.03 MPa @Strain 1.06 %, Temperature 90.0 °C | 6531 psi @Strain 1.06 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 45.1 MPa @Strain 2.91 %, Temperature 150 °C | 6540 psi @Strain 2.91 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 45.77 MPa @Strain 3.76 %, Temperature 180 °C | 6638 psi @Strain 3.76 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 45.87 MPa @Strain 2.04 %, Temperature 120 °C | 6653 psi @Strain 2.04 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 45.92 MPa @Strain 0.760 %, Temperature 23.0 °C | 6660 psi @Strain 0.760 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.42 MPa @Strain 0.420 %, Temperature -20.0 °C | 6733 psi @Strain 0.420 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.43 MPa @Strain 0.400 %, Temperature 23.0 °C | 6734 psi @Strain 0.400 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 46.54 MPa @Strain 1.80 %, Temperature 150 °C | 6750 psi @Strain 1.80 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 46.96 MPa @Strain 3.23 %, Temperature 150 °C | 6811 psi @Strain 3.23 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.37 MPa @Strain 1.13 %, Temperature 60.0 °C | 6870 psi @Strain 1.13 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.52 MPa @Strain 4.16 %, Temperature 180 °C | 6892 psi @Strain 4.16 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 47.95 MPa @Strain 1.63 %, Temperature 90.0 °C | 6955 psi @Strain 1.63 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.99 MPa @Strain 1.42 %, Temperature 120 °C | 6960 psi @Strain 1.42 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 48.68 MPa @Strain 3.56 %, Temperature 150 °C | 7060 psi @Strain 3.56 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.94 MPa @Strain 0.810 %, Temperature 60.0 °C | 7098 psi @Strain 0.810 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 49.14 MPa @Strain 4.51 %, Temperature 180 °C | 7127 psi @Strain 4.51 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 49.22 MPa @Strain 2.35 %, Temperature 120 °C | 7139 psi @Strain 2.35 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 49.75 MPa @Strain 0.530 %, Temperature 40.0 °C | 7216 psi @Strain 0.530 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 49.9 MPa @Strain 1.05 %, Temperature 40.0 °C | 7240 psi @Strain 1.05 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.19 MPa @Strain 3.89 %, Temperature 150 °C | 7279 psi @Strain 3.89 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.56 MPa @Strain 4.93 %, Temperature 180 °C | 7333 psi @Strain 4.93 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 50.79 MPa @Strain 2.17 %, Temperature 150 °C | 7366 psi @Strain 2.17 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 51.59 MPa @Strain 4.22 %, Temperature 150 °C | 7483 psi @Strain 4.22 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.98 MPa @Strain 5.32 %, Temperature 180 °C | 7539 psi @Strain 5.32 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 52.16 MPa @Strain 0.540 %, Temperature 0.000 °C | 7565 psi @Strain 0.540 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 52.16 MPa @Strain 0.400 %, Temperature -20.0 °C | 7565 psi @Strain 0.400 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 52.26 MPa @Strain 2.67 %, Temperature 120 °C | 7580 psi @Strain 2.67 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 52.64 MPa @Strain 1.93 %, Temperature 90.0 °C | 7635 psi @Strain 1.93 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 52.85 MPa @Strain 4.52 %, Temperature 150 °C | 7665 psi @Strain 4.52 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 53.23 MPa @Strain 5.75 %, Temperature 180 °C | 7720 psi @Strain 5.75 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 53.38 MPa @Strain 1.37 %, Temperature 60.0 °C | 7742 psi @Strain 1.37 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 53.91 MPa @Strain 0.940 %, Temperature 23.0 °C | 7819 psi @Strain 0.940 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 53.93 MPa @Strain 4.87 %, Temperature 150 °C | 7822 psi @Strain 4.87 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 53.98 MPa @Strain 1.75 %, Temperature 120 °C | 7829 psi @Strain 1.75 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 53.99 MPa @Strain 1.37 %, Temperature 90.0 °C | 7831 psi @Strain 1.37 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 54.35 MPa @Strain 6.19 %, Temperature 180 °C | 7883 psi @Strain 6.19 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 54.69 MPa @Strain 2.57 %, Temperature 150 °C | 7932 psi @Strain 2.57 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 54.91 MPa @Strain 5.25 %, Temperature 150 °C | 7964 psi @Strain 5.25 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 54.99 MPa @Strain 3.00 %, Temperature 120 °C | 7976 psi @Strain 3.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 55.41 MPa @Strain 6.62 %, Temperature 180 °C | 8037 psi @Strain 6.62 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 55.79 MPa @Strain 5.63 %, Temperature 150 °C | 8092 psi @Strain 5.63 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 55.97 MPa @Strain 0.490 %, Temperature 0.000 °C | 8118 psi @Strain 0.490 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 56.47 MPa @Strain 7.05 %, Temperature 180 °C | 8190 psi @Strain 7.05 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 56.53 MPa @Strain 6.02 %, Temperature 150 °C | 8199 psi @Strain 6.02 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 56.8 MPa @Strain 2.23 %, Temperature 90.0 °C | 8240 psi @Strain 2.23 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 56.91 MPa @Strain 6.82 %, Temperature 150 °C | 8254 psi @Strain 6.82 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 56.94 MPa @Strain 1.28 %, Temperature 40.0 °C | 8258 psi @Strain 1.28 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.09 MPa @Strain 6.40 %, Temperature 150 °C | 8280 psi @Strain 6.40 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.4 MPa @Strain 7.47 %, Temperature 180 °C | 8330 psi @Strain 7.47 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 57.47 MPa @Strain 3.34 %, Temperature 120 °C | 8335 psi @Strain 3.34 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.66 MPa @Strain 8.34 %, Temperature 180 °C | 8363 psi @Strain 8.34 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 57.9 MPa @Strain 2.96 %, Temperature 150 °C | 8400 psi @Strain 2.96 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 58.23 MPa @Strain 7.88 %, Temperature 180 °C | 8446 psi @Strain 7.88 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 58.94 MPa @Strain 1.61 %, Temperature 60.0 °C | 8549 psi @Strain 1.61 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 59.15 MPa @Strain 2.09 %, Temperature 120 °C | 8579 psi @Strain 2.09 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 59.64 MPa @Strain 3.69 %, Temperature 120 °C | 8650 psi @Strain 3.69 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 60.07 MPa @Strain 1.06 %, Temperature 60.0 °C | 8712 psi @Strain 1.06 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 60.3 MPa @Strain 2.52 %, Temperature 90.0 °C | 8750 psi @Strain 2.52 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 60.9 MPa @Strain 3.36 %, Temperature 150 °C | 8830 psi @Strain 3.36 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 61.36 MPa @Strain 0.550 %, Temperature -20.0 °C | 8900 psi @Strain 0.550 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 61.37 MPa @Strain 1.68 %, Temperature 90.0 °C | 8901 psi @Strain 1.68 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 61.61 MPa @Strain 4.04 %, Temperature 120 °C | 8936 psi @Strain 4.04 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 61.92 MPa @Strain 0.540 %, Temperature 23.0 °C | 8981 psi @Strain 0.540 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 62.05 MPa @Strain 1.16 %, Temperature 23.0 °C | 9000 psi @Strain 1.16 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.17 MPa @Strain 0.690 %, Temperature 40.0 °C | 9162 psi @Strain 0.690 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 63.34 MPa @Strain 4.36 %, Temperature 120 °C | 9187 psi @Strain 4.36 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.52 MPa @Strain 3.75 %, Temperature 150 °C | 9213 psi @Strain 3.75 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 63.66 MPa @Strain 2.84 %, Temperature 90.0 °C | 9233 psi @Strain 2.84 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.75 MPa @Strain 1.53 %, Temperature 40.0 °C | 9246 psi @Strain 1.53 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.92 MPa @Strain 2.46 %, Temperature 120 °C | 9271 psi @Strain 2.46 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 64.19 MPa @Strain 1.88 %, Temperature 60.0 °C | 9310 psi @Strain 1.88 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 64.62 MPa @Strain 0.690 %, Temperature 0.000 °C | 9372 psi @Strain 0.690 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 64.88 MPa @Strain 4.73 %, Temperature 120 °C | 9410 psi @Strain 4.73 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 66.03 MPa @Strain 4.13 %, Temperature 150 °C | 9577 psi @Strain 4.13 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 66.26 MPa @Strain 5.14 %, Temperature 120 °C | 9610 psi @Strain 5.14 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 66.78 MPa @Strain 3.19 %, Temperature 90.0 °C | 9686 psi @Strain 3.19 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 67.45 MPa @Strain 5.56 %, Temperature 120 °C | 9783 psi @Strain 5.56 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 68.04 MPa @Strain 2.01 %, Temperature 90.0 °C | 9868 psi @Strain 2.01 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 68.08 MPa @Strain 7.42 %, Temperature 120 °C | 9874 psi @Strain 7.42 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 68.24 MPa @Strain 2.83 %, Temperature 120 °C | 9897 psi @Strain 2.83 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 68.28 MPa @Strain 4.57 %, Temperature 150 °C | 9903 psi @Strain 4.57 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 68.45 MPa @Strain 6.00 %, Temperature 120 °C | 9928 psi @Strain 6.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 69.22 MPa @Strain 6.43 %, Temperature 120 °C | 10040 psi @Strain 6.43 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 69.23 MPa @Strain 2.17 %, Temperature 60.0 °C | 10040 psi @Strain 2.17 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 69.24 MPa @Strain 1.31 %, Temperature 60.0 °C | 10040 psi @Strain 1.31 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 69.53 MPa @Strain 3.55 %, Temperature 90.0 °C | 10080 psi @Strain 3.55 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 69.74 MPa @Strain 6.88 %, Temperature 120 °C | 10110 psi @Strain 6.88 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 69.79 MPa @Strain 1.38 %, Temperature 23.0 °C | 10120 psi @Strain 1.38 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 70.23 MPa @Strain 1.80 %, Temperature 40.0 °C | 10190 psi @Strain 1.80 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 70.26 MPa @Strain 5.00 %, Temperature 150 °C | 10190 psi @Strain 5.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 70.53 MPa @Strain 0.620 %, Temperature 0.000 °C | 10230 psi @Strain 0.620 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 70.99 MPa @Strain 0.560 %, Temperature -20.0 °C | 10300 psi @Strain 0.560 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 71.85 MPa @Strain 3.91 %, Temperature 90.0 °C | 10420 psi @Strain 3.91 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 72.12 MPa @Strain 5.48 %, Temperature 150 °C | 10460 psi @Strain 5.48 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 72.15 MPa @Strain 3.24 %, Temperature 120 °C | 10460 psi @Strain 3.24 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 73.26 MPa @Strain 0.650 %, Temperature -20.0 °C | 10630 psi @Strain 0.650 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.73 MPa @Strain 5.94 %, Temperature 150 °C | 10690 psi @Strain 5.94 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 73.77 MPa @Strain 2.47 %, Temperature 60.0 °C | 10700 psi @Strain 2.47 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.95 MPa @Strain 4.24 %, Temperature 90.0 °C | 10730 psi @Strain 4.24 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 74.02 MPa @Strain 2.36 %, Temperature 90.0 °C | 10740 psi @Strain 2.36 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 74.79 MPa @Strain 0.840 %, Temperature 40.0 °C | 10850 psi @Strain 0.840 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 75.23 MPa @Strain 6.41 %, Temperature 150 °C | 10910 psi @Strain 6.41 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 75.42 MPa @Strain 0.830 %, Temperature 0.000 °C | 10940 psi @Strain 0.830 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 75.64 MPa @Strain 3.64 %, Temperature 120 °C | 10970 psi @Strain 3.64 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 75.75 MPa @Strain 4.63 %, Temperature 90.0 °C | 10990 psi @Strain 4.63 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 76.29 MPa @Strain 2.08 %, Temperature 40.0 °C | 11060 psi @Strain 2.08 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 76.34 MPa @Strain 0.670 %, Temperature 23.0 °C | 11070 psi @Strain 0.670 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 76.54 MPa @Strain 6.87 %, Temperature 150 °C | 11100 psi @Strain 6.87 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 77.0 MPa @Strain 1.61 %, Temperature 23.0 °C | 11200 psi @Strain 1.61 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.34 MPa @Strain 5.07 %, Temperature 90.0 °C | 11220 psi @Strain 5.07 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.59 MPa @Strain 7.32 %, Temperature 150 °C | 11250 psi @Strain 7.32 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 77.73 MPa @Strain 1.55 %, Temperature 60.0 °C | 11270 psi @Strain 1.55 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 77.89 MPa @Strain 2.80 %, Temperature 60.0 °C | 11300 psi @Strain 2.80 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 78.52 MPa @Strain 7.82 %, Temperature 150 °C | 11390 psi @Strain 7.82 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 78.6 MPa @Strain 5.48 %, Temperature 90.0 °C | 11400 psi @Strain 5.48 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 78.76 MPa @Strain 8.94 %, Temperature 150 °C | 11420 psi @Strain 8.94 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 78.78 MPa @Strain 4.05 %, Temperature 120 °C | 11430 psi @Strain 4.05 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 79.21 MPa @Strain 8.32 %, Temperature 150 °C | 11490 psi @Strain 8.32 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 79.39 MPa @Strain 2.71 %, Temperature 90.0 °C | 11510 psi @Strain 2.71 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 79.72 MPa @Strain 5.94 %, Temperature 90.0 °C | 11560 psi @Strain 5.94 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 80.15 MPa @Strain 7.41 %, Temperature 90.0 °C | 11620 psi @Strain 7.41 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 80.56 MPa @Strain 6.42 %, Temperature 90.0 °C | 11680 psi @Strain 6.42 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 81.08 MPa @Strain 6.86 %, Temperature 90.0 °C | 11760 psi @Strain 6.86 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 81.6 MPa @Strain 4.46 %, Temperature 120 °C | 11800 psi @Strain 4.46 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 81.62 MPa @Strain 3.14 %, Temperature 60.0 °C | 11840 psi @Strain 3.14 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 81.87 MPa @Strain 2.38 %, Temperature 40.0 °C | 11870 psi @Strain 2.38 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 83.18 MPa @Strain 0.730 %, Temperature 0.000 °C | 12060 psi @Strain 0.730 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 84.09 MPa @Strain 4.90 %, Temperature 120 °C | 12200 psi @Strain 4.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 84.17 MPa @Strain 1.87 %, Temperature 23.0 °C | 12210 psi @Strain 1.87 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 84.28 MPa @Strain 3.09 %, Temperature 90.0 °C | 12220 psi @Strain 3.09 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 84.86 MPa @Strain 3.47 %, Temperature 60.0 °C | 12310 psi @Strain 3.47 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 85.22 MPa @Strain 0.770 %, Temperature -20.0 °C | 12360 psi @Strain 0.770 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 85.27 MPa @Strain 1.00 %, Temperature 40.0 °C | 12370 psi @Strain 1.00 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 85.34 MPa @Strain 0.990 %, Temperature 0.000 °C | 12380 psi @Strain 0.990 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 85.43 MPa @Strain 1.81 %, Temperature 60.0 °C | 12390 psi @Strain 1.81 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 85.97 MPa @Strain 0.690 %, Temperature -20.0 °C | 12470 psi @Strain 0.690 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 86.35 MPa @Strain 5.39 %, Temperature 120 °C | 12520 psi @Strain 5.39 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 87.0 MPa @Strain 2.71 %, Temperature 40.0 °C | 12600 psi @Strain 2.71 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 87.64 MPa @Strain 3.85 %, Temperature 60.0 °C | 12710 psi @Strain 3.85 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 88.29 MPa @Strain 5.90 %, Temperature 120 °C | 12810 psi @Strain 5.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 88.65 MPa @Strain 3.49 %, Temperature 90.0 °C | 12860 psi @Strain 3.49 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 89.84 MPa @Strain 0.800 %, Temperature 23.0 °C | 13030 psi @Strain 0.800 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 89.99 MPa @Strain 6.41 %, Temperature 120 °C | 13050 psi @Strain 6.41 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 90.02 MPa @Strain 4.30 %, Temperature 60.0 °C | 13060 psi @Strain 4.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 90.74 MPa @Strain 2.15 %, Temperature 23.0 °C | 13160 psi @Strain 2.15 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.49 MPa @Strain 3.06 %, Temperature 40.0 °C | 13270 psi @Strain 3.06 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.51 MPa @Strain 6.93 %, Temperature 120 °C | 13270 psi @Strain 6.93 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 91.96 MPa @Strain 4.75 %, Temperature 60.0 °C | 13340 psi @Strain 4.75 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 92.59 MPa @Strain 3.90 %, Temperature 90.0 °C | 13430 psi @Strain 3.90 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 92.72 MPa @Strain 7.45 %, Temperature 120 °C | 13450 psi @Strain 7.45 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 92.74 MPa @Strain 2.09 %, Temperature 60.0 °C | 13450 psi @Strain 2.09 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 93.55 MPa @Strain 5.21 %, Temperature 60.0 °C | 13570 psi @Strain 5.21 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 93.73 MPa @Strain 7.98 %, Temperature 120 °C | 13590 psi @Strain 7.98 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 94.07 MPa @Strain 9.25 %, Temperature 120 °C | 13640 psi @Strain 9.25 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 94.28 MPa @Strain 7.42 %, Temperature 60.0 °C | 13670 psi @Strain 7.42 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 94.43 MPa @Strain 8.57 %, Temperature 120 °C | 13700 psi @Strain 8.57 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 94.78 MPa @Strain 5.71 %, Temperature 60.0 °C | 13750 psi @Strain 5.71 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 95.07 MPa @Strain 1.15 %, Temperature 0.000 °C | 13790 psi @Strain 1.15 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 95.19 MPa @Strain 1.16 %, Temperature 40.0 °C | 13810 psi @Strain 1.16 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 95.45 MPa @Strain 3.38 %, Temperature 40.0 °C | 13840 psi @Strain 3.38 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 95.64 MPa @Strain 6.20 %, Temperature 60.0 °C | 13870 psi @Strain 6.20 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 95.99 MPa @Strain 4.31 %, Temperature 90.0 °C | 13920 psi @Strain 4.31 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 96.08 MPa @Strain 6.74 %, Temperature 60.0 °C | 13940 psi @Strain 6.74 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 96.23 MPa @Strain 0.860 %, Temperature 0.000 °C | 13960 psi @Strain 0.860 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 96.54 MPa @Strain 2.42 %, Temperature 23.0 °C | 14000 psi @Strain 2.42 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 97.86 MPa @Strain 0.900 %, Temperature -20.0 °C | 14190 psi @Strain 0.900 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 98.74 MPa @Strain 3.78 %, Temperature 40.0 °C | 14320 psi @Strain 3.78 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 98.96 MPa @Strain 4.79 %, Temperature 90.0 °C | 14350 psi @Strain 4.79 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 99.3 MPa @Strain 2.38 %, Temperature 60.0 °C | 14400 psi @Strain 2.38 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 100.86 MPa @Strain 0.840 %, Temperature -20.0 °C | 14629 psi @Strain 0.840 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 101.24 MPa @Strain 0.930 %, Temperature 23.0 °C | 14684 psi @Strain 0.930 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 101.44 MPa @Strain 4.22 %, Temperature 40.0 °C | 14713 psi @Strain 4.22 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 101.51 MPa @Strain 5.30 %, Temperature 90.0 °C | 14723 psi @Strain 5.30 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 102.22 MPa @Strain 2.73 %, Temperature 23.0 °C | 14826 psi @Strain 2.73 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 103.59 MPa @Strain 5.81 %, Temperature 90.0 °C | 15024 psi @Strain 5.81 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 103.6 MPa @Strain 4.68 %, Temperature 40.0 °C | 15030 psi @Strain 4.68 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 104.32 MPa @Strain 1.31 %, Temperature 0.000 °C | 15130 psi @Strain 1.31 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 104.43 MPa @Strain 1.32 %, Temperature 40.0 °C | 15146 psi @Strain 1.32 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 105.38 MPa @Strain 5.18 %, Temperature 40.0 °C | 15284 psi @Strain 5.18 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 105.38 MPa @Strain 2.68 %, Temperature 60.0 °C | 15284 psi @Strain 2.68 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 105.39 MPa @Strain 6.36 %, Temperature 90.0 °C | 15286 psi @Strain 6.36 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 105.6 MPa @Strain 7.51 %, Temperature 40.0 °C | 15320 psi @Strain 7.51 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 106.63 MPa @Strain 5.67 %, Temperature 40.0 °C | 15465 psi @Strain 5.67 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 106.82 MPa @Strain 6.91 %, Temperature 90.0 °C | 15493 psi @Strain 6.91 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 107.18 MPa @Strain 3.05 %, Temperature 23.0 °C | 15545 psi @Strain 3.05 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 107.49 MPa @Strain 6.20 %, Temperature 40.0 °C | 15590 psi @Strain 6.20 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 107.84 MPa @Strain 6.80 %, Temperature 40.0 °C | 15641 psi @Strain 6.80 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 107.95 MPa @Strain 7.47 %, Temperature 90.0 °C | 15657 psi @Strain 7.47 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 108.46 MPa @Strain 9.42 %, Temperature 90.0 °C | 15731 psi @Strain 9.42 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 108.8 MPa @Strain 8.06 %, Temperature 90.0 °C | 15780 psi @Strain 8.06 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 108.95 MPa @Strain 0.990 %, Temperature 0.000 °C | 15802 psi @Strain 0.990 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 109.19 MPa @Strain 8.70 %, Temperature 90.0 °C | 15837 psi @Strain 8.70 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 110.27 MPa @Strain 1.04 %, Temperature -20.0 °C | 15993 psi @Strain 1.04 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 110.88 MPa @Strain 3.01 %, Temperature 60.0 °C | 16082 psi @Strain 3.01 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 111.42 MPa @Strain 3.43 %, Temperature 23.0 °C | 16160 psi @Strain 3.43 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 112.55 MPa @Strain 1.05 %, Temperature 23.0 °C | 16324 psi @Strain 1.05 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 113.04 MPa @Strain 1.49 %, Temperature 0.000 °C | 16395 psi @Strain 1.49 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 113.33 MPa @Strain 1.49 %, Temperature 40.0 °C | 16437 psi @Strain 1.49 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 114.84 MPa @Strain 3.84 %, Temperature 23.0 °C | 16656 psi @Strain 3.84 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 115.73 MPa @Strain 3.35 %, Temperature 60.0 °C | 16785 psi @Strain 3.35 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 116.05 MPa @Strain 0.980 %, Temperature -20.0 °C | 16832 psi @Strain 0.980 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 117.4 MPa @Strain 4.24 %, Temperature 23.0 °C | 17030 psi @Strain 4.24 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 119.4 MPa @Strain 4.70 %, Temperature 23.0 °C | 17320 psi @Strain 4.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 119.89 MPa @Strain 3.72 %, Temperature 60.0 °C | 17389 psi @Strain 3.72 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 120.28 MPa @Strain 7.05 %, Temperature 23.0 °C | 17445 psi @Strain 7.05 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 120.82 MPa @Strain 5.19 %, Temperature 23.0 °C | 17523 psi @Strain 5.19 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 121.35 MPa @Strain 1.67 %, Temperature 0.000 °C | 17600 psi @Strain 1.67 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 121.66 MPa @Strain 5.75 %, Temperature 23.0 °C | 17645 psi @Strain 5.75 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 121.8 MPa @Strain 1.19 %, Temperature -20.0 °C | 17670 psi @Strain 1.19 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 121.83 MPa @Strain 1.69 %, Temperature 40.0 °C | 17670 psi @Strain 1.69 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 121.88 MPa @Strain 1.13 %, Temperature 0.000 °C | 17677 psi @Strain 1.13 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 121.95 MPa @Strain 6.34 %, Temperature 23.0 °C | 17687 psi @Strain 6.34 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 123.15 MPa @Strain 1.18 %, Temperature 23.0 °C | 17861 psi @Strain 1.18 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 123.25 MPa @Strain 4.09 %, Temperature 60.0 °C | 17876 psi @Strain 4.09 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 125.93 MPa @Strain 4.54 %, Temperature 60.0 °C | 18265 psi @Strain 4.54 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 128.04 MPa @Strain 5.01 %, Temperature 60.0 °C | 18571 psi @Strain 5.01 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 129.33 MPa @Strain 1.88 %, Temperature 0.000 °C | 18758 psi @Strain 1.88 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 129.56 MPa @Strain 5.54 %, Temperature 60.0 °C | 18791 psi @Strain 5.54 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 129.58 MPa @Strain 1.90 %, Temperature 40.0 °C | 18794 psi @Strain 1.90 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 130.55 MPa @Strain 7.82 %, Temperature 60.0 °C | 18935 psi @Strain 7.82 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 130.62 MPa @Strain 6.08 %, Temperature 60.0 °C | 18945 psi @Strain 6.08 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 131.29 MPa @Strain 1.13 %, Temperature -20.0 °C | 19042 psi @Strain 1.13 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 131.33 MPa @Strain 6.62 %, Temperature 60.0 °C | 19048 psi @Strain 6.62 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 131.56 MPa @Strain 7.19 %, Temperature 60.0 °C | 19081 psi @Strain 7.19 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 132.76 MPa @Strain 1.33 %, Temperature -20.0 °C | 19255 psi @Strain 1.33 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 133.04 MPa @Strain 1.30 %, Temperature 23.0 °C | 19296 psi @Strain 1.30 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 134.08 MPa @Strain 1.27 %, Temperature 0.000 °C | 19447 psi @Strain 1.27 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 136.66 MPa @Strain 2.08 %, Temperature 0.000 °C | 19821 psi @Strain 2.08 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 136.83 MPa @Strain 2.12 %, Temperature 40.0 °C | 19846 psi @Strain 2.12 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 142.92 MPa @Strain 1.44 %, Temperature 23.0 °C | 20729 psi @Strain 1.44 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 143.36 MPa @Strain 2.36 %, Temperature 40.0 °C | 20793 psi @Strain 2.36 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 143.42 MPa @Strain 2.30 %, Temperature 0.000 °C | 20801 psi @Strain 2.30 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 143.73 MPa @Strain 1.49 %, Temperature -20.0 °C | 20846 psi @Strain 1.49 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 145.29 MPa @Strain 1.40 %, Temperature 0.000 °C | 21073 psi @Strain 1.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 145.84 MPa @Strain 1.30 %, Temperature -20.0 °C | 21152 psi @Strain 1.30 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 149.11 MPa @Strain 2.64 %, Temperature 40.0 °C | 21627 psi @Strain 2.64 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 149.69 MPa @Strain 2.54 %, Temperature 0.000 °C | 21711 psi @Strain 2.54 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 152.88 MPa @Strain 1.60 %, Temperature 23.0 °C | 22173 psi @Strain 1.60 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 153.76 MPa @Strain 2.94 %, Temperature 40.0 °C | 22301 psi @Strain 2.94 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 154.17 MPa @Strain 1.65 %, Temperature -20.0 °C | 22361 psi @Strain 1.65 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 155.12 MPa @Strain 2.80 %, Temperature 0.000 °C | 22498 psi @Strain 2.80 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 156.52 MPa @Strain 1.55 %, Temperature 0.000 °C | 22701 psi @Strain 1.55 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 157.42 MPa @Strain 3.28 %, Temperature 40.0 °C | 22832 psi @Strain 3.28 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 159.32 MPa @Strain 5.07 %, Temperature 40.0 °C | 23107 psi @Strain 5.07 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 159.54 MPa @Strain 3.10 %, Temperature 0.000 °C | 23139 psi @Strain 3.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 159.7 MPa @Strain 3.65 %, Temperature 40.0 °C | 23160 psi @Strain 3.65 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 159.95 MPa @Strain 1.46 %, Temperature -20.0 °C | 23199 psi @Strain 1.46 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 160.67 MPa @Strain 4.05 %, Temperature 40.0 °C | 23303 psi @Strain 4.05 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 160.68 MPa @Strain 4.51 %, Temperature 40.0 °C | 23305 psi @Strain 4.51 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 161.31 MPa @Strain 4.85 %, Temperature 0.000 °C | 23396 psi @Strain 4.85 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 162.12 MPa @Strain 1.75 %, Temperature 23.0 °C | 23514 psi @Strain 1.75 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 162.63 MPa @Strain 3.42 %, Temperature 0.000 °C | 23588 psi @Strain 3.42 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 164 MPa @Strain 4.30 %, Temperature 0.000 °C | 23800 psi @Strain 4.30 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 164.12 MPa @Strain 3.82 %, Temperature 0.000 °C | 23804 psi @Strain 3.82 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 164.28 MPa @Strain 1.83 %, Temperature -20.0 °C | 23827 psi @Strain 1.83 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 167.43 MPa @Strain 1.71 %, Temperature 0.000 °C | 24284 psi @Strain 1.71 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 171.1 MPa @Strain 1.94 %, Temperature 23.0 °C | 24820 psi @Strain 1.94 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 173.69 MPa @Strain 1.62 %, Temperature -20.0 °C | 25192 psi @Strain 1.62 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 174.04 MPa @Strain 2.02 %, Temperature -20.0 °C | 25242 psi @Strain 2.02 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 178.11 MPa @Strain 1.87 %, Temperature 0.000 °C | 25833 psi @Strain 1.87 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 179.12 MPa @Strain 2.12 %, Temperature 23.0 °C | 25979 psi @Strain 2.12 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 182.85 MPa @Strain 2.22 %, Temperature -20.0 °C | 26520 psi @Strain 2.22 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 186.46 MPa @Strain 2.34 %, Temperature 23.0 °C | 27044 psi @Strain 2.34 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 186.9 MPa @Strain 1.80 %, Temperature -20.0 °C | 27110 psi @Strain 1.80 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 188.32 MPa @Strain 2.05 %, Temperature 0.000 °C | 27314 psi @Strain 2.05 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 190.8 MPa @Strain 2.43 %, Temperature -20.0 °C | 27670 psi @Strain 2.43 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 192.96 MPa @Strain 2.59 %, Temperature 23.0 °C | 27987 psi @Strain 2.59 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 197.94 MPa @Strain 2.88 %, Temperature 23.0 °C | 28709 psi @Strain 2.88 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 198.09 MPa @Strain 2.67 %, Temperature -20.0 °C | 28731 psi @Strain 2.67 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 198.14 MPa @Strain 2.25 %, Temperature 0.000 °C | 28738 psi @Strain 2.25 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 199.33 MPa @Strain 1.98 %, Temperature -20.0 °C | 28910 psi @Strain 1.98 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 199.44 MPa @Strain 3.72 %, Temperature 23.0 °C | 28926 psi @Strain 3.72 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 200.78 MPa @Strain 3.22 %, Temperature 23.0 °C | 29121 psi @Strain 3.22 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 204.06 MPa @Strain 2.88 %, Temperature -20.0 °C | 29596 psi @Strain 2.88 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 206.92 MPa @Strain 2.46 %, Temperature 0.000 °C | 30011 psi @Strain 2.46 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 208.19 MPa @Strain 3.20 %, Temperature -20.0 °C | 30195 psi @Strain 3.20 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 208.63 MPa @Strain 3.67 %, Temperature -20.0 °C | 30259 psi @Strain 3.67 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 211.56 MPa @Strain 2.17 %, Temperature -20.0 °C | 30684 psi @Strain 2.17 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 214.64 MPa @Strain 2.65 %, Temperature 0.000 °C | 31131 psi @Strain 2.65 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 221.59 MPa @Strain 2.89 %, Temperature 0.000 °C | 32139 psi @Strain 2.89 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 223.08 MPa @Strain 2.38 %, Temperature -20.0 °C | 32355 psi @Strain 2.38 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 226.74 MPa @Strain 3.21 %, Temperature 0.000 °C | 32886 psi @Strain 3.21 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 228.31 MPa @Strain 3.63 %, Temperature 0.000 °C | 33114 psi @Strain 3.63 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 233.99 MPa @Strain 2.54 %, Temperature -20.0 °C | 33937 psi @Strain 2.54 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 244.28 MPa @Strain 2.77 %, Temperature -20.0 °C | 35430 psi @Strain 2.77 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 253.45 MPa @Strain 3.01 %, Temperature -20.0 °C | 36760 psi @Strain 3.01 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 261.7 MPa @Strain 3.29 %, Temperature -20.0 °C | 37960 psi @Strain 3.29 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 268.29 MPa @Strain 3.59 %, Temperature -20.0 °C | 38912 psi @Strain 3.59 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| Elongation at Break | 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 7.0 % @Temperature 23.0 °C | 7.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 6.50 GPa @Temperature 23.0 °C | 943 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 11.5 GPa @Temperature 23.0 °C | 1670 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 309 MPa @Temperature 23.0 °C | 44800 psi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Flexural Modulus | 10.1 GPa @Temperature 23.0 °C | 1460 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Charpy Impact Unnotched | 8.10 J/cm2 @Temperature -30.0 °C | 38.5 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| 8.30 J/cm2 @Temperature -30.0 °C | 39.5 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| 9.30 J/cm2 @Temperature 23.0 °C | 44.3 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| 9.60 J/cm2 @Temperature 23.0 °C | 45.7 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm2 @Temperature -30.0 °C | 6.19 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 7.10e+13 ohm-cm @Temperature 23.0 °C | 7.10e+13 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 1.40e+16 ohm-cm @Temperature 23.0 °C | 1.40e+16 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | 6.10e+13 ohm @Temperature 23.0 °C | 6.10e+13 ohm @Temperature 73.4 °F | DAM; IEC 60093 | ||
| 1.00e+15 ohm @Temperature 23.0 °C | 1.00e+15 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | |||
| Comparative Tracking Index | 550 V @Temperature 23.0 °C | 550 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 10.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 5.56 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 224 °C | 435 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 270 °C | 518 °F | DAM; Optimum | |||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Flow, Good | DAM | |||
| Weldable | DAM | ||||
| Filler | Glass Reinforced | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA6-GF35< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA6 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| SHIELD Technology Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA6-GF35 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Automotive Applications | DAM | |||
| Automotive Under the Hood | DAM | ||||
| High Temperature Applications | DAM | ||||