- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 1.7
- 缺口沖擊強度: 18.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 1.7 % @Temperature 23.0 °C | 1.7 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 5.4 % @Temperature 23.0 °C | 5.4 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 2.00 mm | 0.0060 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 128 MPa @Temperature 23.0 °C | 18600 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 185 MPa @Temperature 23.0 °C | 26800 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 7.3 % @Temperature 23.0 °C | 7.3 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Elongation at Yield | 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 22 % @Temperature 23.0 °C | 22 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 7.50 GPa @Temperature 23.0 °C | 1090 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 12.2 GPa @Temperature 23.0 °C | 1770 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 18.0 kJ/m2 @Temperature -30.0 °C | 8.57 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 180/1A | ||
| 19.0 kJ/m2 @Temperature -30.0 °C | 9.04 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 24.0 kJ/m2 @Temperature 23.0 °C | 11.4 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 30.0 kJ/m2 @Temperature 23.0 °C | 14.3 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 10.5 J/cm2 @Temperature -30.0 °C | 50.0 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| 11.0 J/cm2 @Temperature 23.0 °C | 52.3 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 11.3 J/cm2 @Temperature 23.0 °C | 53.8 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| 11.8 J/cm2 @Temperature -30.0 °C | 56.1 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.70 J/cm2 @Temperature -30.0 °C | 8.09 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 1.80 J/cm2 @Temperature -30.0 °C | 8.57 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
| 2.40 J/cm2 @Temperature 23.0 °C | 11.4 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 3.30 J/cm2 @Temperature 23.0 °C | 15.7 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| 270 °C | 518 °F | DAM; Optimum | |||
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | DAM | ||
| 80.0 °C | 176 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Forms | Pellets | DAM | |||
| Generic | PA66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Toughened Resins | DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||