- 密度 [g/cm3]: 1.18
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 15 % | 15 % | DAM | ||
| Linear Mold Shrinkage, Flow | 0.0028 cm/cm @Thickness 2.00 mm | 0.0028 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 65.0 MPa @Temperature 23.0 °C | 9430 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 107 MPa @Temperature 23.0 °C | 15500 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 5.7 % @Temperature 23.0 °C | 5.7 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 22 % @Temperature 23.0 °C | 22 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 2.50 GPa @Temperature 23.0 °C | 363 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 5.10 GPa @Temperature 23.0 °C | 740 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Charpy Impact Unnotched | 8.50 J/cm2 @Temperature 23.0 °C | 40.4 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| 11.5 J/cm2 @Temperature 23.0 °C | 54.7 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 2.70 J/cm2 @Temperature 23.0 °C | 12.8 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 3.30 J/cm2 @Temperature 23.0 °C | 15.7 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 270 °C | 518 °F | DAM; Optimum | |||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | DAM | ||
| 80.0 °C | 176 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.030 % | <= 0.030 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA6-IGF15< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA6 | DAM | |||
| Processing Method | Blow Molding | DAM | |||
| Product Category | Blow Moldable Resins | DAM | |||
| Glass Reinforced Resins | DAM | ||||
| Toughened Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA6-IGF15 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||