- 密度 [g/cm3]: 1.36
- 缺口沖擊強度: 13.0
- 彎曲模量 [MPa]: 6.00
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 30 % | 30 % | DAM | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C | 16000 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 180 MPa @Temperature 23.0 °C | 26100 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 5.70 GPa @Temperature 23.0 °C | 827 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 9.50 GPa @Temperature 23.0 °C | 1380 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 6.00 GPa @Temperature 23.0 °C | 870 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 9.00 GPa @Temperature 23.0 °C | 1310 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched (ISO) | 13.0 kJ/m2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 18.0 kJ/m2 @Temperature 23.0 °C | 8.57 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 8.50 J/cm2 @Temperature 23.0 °C | 40.4 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| 9.00 J/cm2 @Temperature 23.0 °C | 42.8 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.40 J/cm2 @Temperature 23.0 °C | 6.66 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 2.00 J/cm2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 0.800 mm | 149 °F @Thickness 0.0315 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.800 mm | 149 °F @Thickness 0.0315 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.800 mm | 149 °F @Thickness 0.0315 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 270 °C | 518 °F | DAM; Optimum | |||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA6-GF30< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA6 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Resin Identification | PA6-GF30 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||