- 密度 [g/cm3]: 1.13
- 拉伸強(qiáng)度 [MPa]: 80.0
- 彎曲模量 [MPa]: 2.70
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | DAM; ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 40 % @Temperature 23.0 °C | 40 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | ||
| Elongation at Yield | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 2.90 GPa @Temperature 23.0 °C | 421 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 2.70 GPa @Temperature 23.0 °C | 392 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Charpy Impact, Notched | 0.500 J/cm2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | DAM; ISO 75-1/-2 | ||
| Flammability, UL94 | V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; IEC 60695-11-10 | ||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | DAM; UL94 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; UL94 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; UL94 | |||
| V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | DAM | ||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA6< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| Resin Identification | PA6 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||