- 吸水率 [%]: 3.0
- 缺口沖擊強度: 0.48
- 拉伸強度 [MPa]: 50.0
- 熱變形溫度 [℃]: 160.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | DAM; ASTM D792 | ||
| Water Absorption | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ASTM D570 | ||
| Linear Mold Shrinkage | 0.012 cm/cm @Thickness 3.20 mm | 0.012 in/in @Thickness 0.126 in | Flow; DAM | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 50.0 MPa @Temperature 23.0 °C | 7250 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Tensile Modulus | 1.50 GPa @Temperature 23.0 °C | 218 ksi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 3.00 GPa @Temperature 23.0 °C | 435 ksi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Izod Impact, Notched | 0.480 J/cm @Temperature -40.0 °C | 0.899 ft-lb/in @Temperature -40.0 °F | DAM; ASTM D256 | ||
| 1.33 J/cm @Temperature 23.0 °C | 2.49 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | |||
| 6.40 J/cm @Temperature 23.0 °C | 12.0 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | DAM; ASTM D648 | ||
| 160 °C | 320 °F | DAM; ISO 75-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DAM; ISO 75-1/-2 | ||
| 65.0 °C | 149 °F | DAM; ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 °C | 428 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 235 °C | 455 °F | DAM; Optimum; Extrusion | |||
| 230 - 240 °C | 446 - 464 °F | DAM; Extrusion | |||
| 260 - 280 °C | 500 - 536 °F | DAM; Injection Molding | |||
| 270 °C | 518 °F | DAM; Optimum; Injection Molding | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum; Injection Molding | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| 80.0 °C | 176 °F | DAM; Injection Molding | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Extrusion | ||
| <= 0.050 % | <= 0.050 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Fuel Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Oil Resistant | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA6< | ISO 11469; DAM | |||
| Processing Method | Extrusion | DAM | |||
| Injection Molding | DAM | ||||
| Product Category | Extrusion Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| Resin Identification | PA6 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| Industrial Applications | DAM | ||||