- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 3.0
- 缺口沖擊強度: 0.62
- 拉伸強度 [MPa]: 41.0
- 彎曲模量 [MPa]: 0.695
- 熱變形溫度 [℃]: 158.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | DAM; ASTM D792 | ||
| Density | 1.13 g/cc | 0.0408 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 9.5 % @Temperature 23.0 °C | 9.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 3.00 mm | 0.010 in/in @Thickness 0.118 in | Flow; DAM | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 60.0 MPa @Temperature 23.0 °C | 8700 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Tensile Strength, Yield | 41.0 MPa @Temperature 23.0 °C | 5950 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 50.0 MPa @Temperature 23.0 °C | 7250 psi @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 50 % @Temperature 23.0 °C | 50 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |||
| 60 % @Temperature 23.0 °C | 60 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| >= 100 % @Temperature 23.0 °C | >= 100 % @Temperature 73.4 °F | 50mm/min; 50%RH; ISO 527 | |||
| 240 % @Temperature 23.0 °C | 240 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| Elongation at Yield | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 4.8 % @Temperature 23.0 °C | 4.8 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| 23 % @Temperature 23.0 °C | 23 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| Tensile Modulus | 1.50 GPa @Temperature 23.0 °C | 218 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 2.90 GPa @Temperature 23.0 °C | 421 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 27.0 MPa @Strain 5.00 %, Temperature 23.0 °C | 3920 psi @Strain 5.00 %, Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 110 MPa @Strain 5.00 %, Temperature 23.0 °C | 16000 psi @Strain 5.00 %, Temperature 73.4 °F | DAM; ASTM D790 | |||
| Flexural Modulus | 0.695 GPa @Temperature 23.0 °C | 101 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 2.30 GPa @Temperature 23.0 °C | 334 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| 2.78 GPa @Temperature 23.0 °C | 403 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Izod Impact, Notched | 0.620 J/cm @Temperature 23.0 °C | 1.16 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| 7.50 J/cm @Temperature 23.0 °C | 14.1 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
| Izod Impact, Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ASTM D4812 | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 @Temperature -40.0 °C | 2.86 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 6.00 kJ/m2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 180/1U | ||
| Charpy Impact Unnotched | NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | DAM; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm @Temperature 23.0 °C | 1.00e+12 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | 1.00e+10 ohm @Temperature 23.0 °C | 1.00e+10 ohm @Temperature 73.4 °F | 50%RH; IEC 60167 | ||
| 1.00e+13 ohm @Temperature 23.0 °C | 1.00e+13 ohm @Temperature 73.4 °F | DAM; IEC 60167 | |||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.5 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 7.0 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 7.0 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | 50%RH; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 100 μm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 100 μm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 220 °C | 428 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | DAM; ASTM D648 | ||
| 160 °C | 320 °F | DAM; ISO 75-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | DAM; ISO 75-1/-2 | ||
| 55.0 °C | 131 °F | DAM; ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 230 °C | 446 °F | DAM; Optimum; Extrusion | |||
| 230 - 240 °C | 446 - 464 °F | DAM; Extrusion | |||
| 260 - 280 °C | 500 - 536 °F | DAM; Injection Molding | |||
| 270 °C | 518 °F | DAM; Optimum; Injection Molding | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum; Injection Molding | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| 80.0 °C | 176 °F | DAM; Injection Molding | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |||
| Moisture Content | <= 0.040 % | <= 0.040 % | DAM; Extrusion | ||
| <= 0.20 % | <= 0.20 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Fuel Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Oil Resistant | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA6< | ISO 11469; DAM | |||
| Processing Method | Extrusion | DAM | |||
| Injection Molding | DAM | ||||
| Product Category | Extrusion Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| Resin Identification | PA6 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| Industrial Applications | DAM | ||||