- 密度 [g/cm3]: 1.06
- 缺口沖擊強度: 13.0
- 拉伸強度 [MPa]: 29.0
- 彎曲模量 [MPa]: 0.570
- 熱變形溫度 [℃]: 95.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 2.00 mm | 0.012 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 29.0 MPa @Temperature 23.0 °C | 4210 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 48.0 MPa @Temperature 23.0 °C | 6960 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; 50mm/min; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; 50mm/min; ISO 527 | |||
| Elongation at Yield | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 30 % @Temperature 23.0 °C | 30 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 0.540 GPa @Temperature 23.0 °C | 78.3 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 1.80 GPa @Temperature 23.0 °C | 261 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 0.570 GPa @Temperature 23.0 °C | 82.7 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 1.70 GPa @Temperature 23.0 °C | 247 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched (ISO) | 13.0 kJ/m2 @Temperature -40.0 °C | 6.19 ft-lb/in2 @Temperature -40.0 °F | 50%RH; ISO 180/1A | ||
| 14.0 kJ/m2 @Temperature -30.0 °C | 6.66 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 15.0 kJ/m2 @Temperature -40.0 °C | 7.14 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 180/1A | |||
| 15.0 kJ/m2 @Temperature -30.0 °C | 7.14 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 180/1A | |||
| 59.0 kJ/m2 @Temperature 23.0 °C | 28.1 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 95.0 kJ/m2 @Temperature 23.0 °C | 45.2 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact, Notched | 1.70 J/cm2 @Temperature -40.0 °C | 8.09 ft-lb/in2 @Temperature -40.0 °F | 50%RH; ISO 179/1eA | ||
| 1.70 J/cm2 @Temperature -30.0 °C | 8.09 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 1.80 J/cm2 @Temperature -30.0 °C | 8.57 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
| 1.80 J/cm2 @Temperature -40.0 °C | 8.57 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 179/1eA | |||
| 2.30 J/cm2 @Temperature -20.0 °C | 10.9 ft-lb/in2 @Temperature -4.00 °F | 50%RH; ISO 179/1eA | |||
| 2.40 J/cm2 @Temperature -20.0 °C | 11.4 ft-lb/in2 @Temperature -4.00 °F | DAM; ISO 179/1eA | |||
| 7.40 J/cm2 @Temperature 0.000 °C | 35.2 ft-lb/in2 @Temperature 32.0 °F | DAM; ISO 179/1eA | |||
| 7.80 J/cm2 @Temperature 23.0 °C | 37.1 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 9.40 J/cm2 @Temperature 0.000 °C | 44.7 ft-lb/in2 @Temperature 32.0 °F | 50%RH; ISO 179/1eA | |||
| 11.8 J/cm2 @Temperature 23.0 °C | 56.1 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 320 MPa @Temperature 23.0 °C | 46400 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 221 °C | 430 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 °C | 464 °F | DAM; optimum; Extrusion | ||
| 235 - 250 °C | 455 - 482 °F | DAM; Extrusion | |||
| 260 - 280 °C | 500 - 536 °F | DAM; Injection Molding | |||
| 270 °C | 518 °F | DAM; optimum; Injection Molding | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; Optimum; Injection Molding | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| 80.0 °C | 176 °F | DAM; Injection Molding | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Dehumidified Dryer; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Dehumidified Dryer; Extrusion | |||
| Moisture Content | <= 0.060 % | <= 0.060 % | DAM; Extrusion | ||
| <= 0.20 % | <= 0.20 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Additive | Impact Modifier | ||||
| Appearance | Natural Color | ||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | ||||
| Features | Chemical Resistance, Good | ||||
| Fuel Resistant | |||||
| Grease Resistant | |||||
| Heat Stabilized | |||||
| Heat Stabilized | |||||
| Impact Modified | |||||
| Impact Resistance, High | |||||
| Lubricated | |||||
| Oil Resistant | |||||
| Toughness, Ultra High | |||||
| Forms | Pellets | ||||
| Generic | Nylon 6 | ||||
| Material Status | Current | ||||
| Part Marking Code | >PA6-HI< | ISO 11469 | |||
| Processing Method | Extrusion | ||||
| Injection Molding | |||||
| Product Category | Extrusion Resins | ||||
| Toughened Resins | |||||
| Unreinforced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PA6-HI | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Appliance Components | ||||
| Automotive Applications | |||||
| Electrical/Electronic Applications | |||||
| Industrial Applications | |||||
| Sporting Goods | |||||