- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 1.9
- 缺口沖擊強度: 10.0
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 30 % | 30 % | DAM | ||
| Water Absorption | 1.9 % @Temperature 23.0 °C | 1.9 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 6.3 % @Temperature 23.0 °C | 6.3 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 2.00 mm | 0.0060 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 482 °F | DAM; cm3/10 min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 115 MPa @Temperature 23.0 °C | 16700 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 185 MPa @Temperature 23.0 °C | 26800 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 5.80 GPa @Temperature 23.0 °C | 841 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 9.70 GPa @Temperature 23.0 °C | 1410 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 180/1A | ||
| 11.0 kJ/m2 @Temperature -30.0 °C | 5.23 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 180/1A | |||
| 15.0 kJ/m2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 20.0 kJ/m2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 8.00 J/cm2 @Temperature -30.0 °C | 38.1 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| 8.40 J/cm2 @Temperature -30.0 °C | 40.0 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| 10.0 J/cm2 @Temperature 23.0 °C | 47.6 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| 10.0 J/cm2 @Temperature 23.0 °C | 47.6 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 1.60 J/cm2 @Temperature 23.0 °C | 7.61 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 2.10 J/cm2 @Temperature -30.0 °C | 9.99 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
| 2.30 J/cm2 @Temperature 23.0 °C | 10.9 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 6190 MPa @Temperature 23.0 °C | 898000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 4630 MPa @Temperature 23.0 °C | 672000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 102 μm/m-°C @Temperature 23.0 - 55.0 °C | 56.7 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 102 μm/m-°C @Temperature 23.0 - 55.0 °C | 56.7 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 65.0 °C | 149 °F | 10°C/min; DAM; ISO 11357-1/-2 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 270 °C | 518 °F | DAM; Optimum | |||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Lubricant | DAM | ||||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Fatigue Resistant | DAM | ||||
| Fuel Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Heat Stabilized | DAM | ||||
| Oil Resistant | DAM | ||||
| Thermal Aging Resistance, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA6-GF30< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA6 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA6-GF30 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| High Gloss Applications | DAM | ||||
| Industrial Applications | DAM | ||||