- 密度 [g/cm3]: 1.13
- 拉伸強度 [MPa]: 23.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 24 Hours; ISO 62 | ||
| 2.7 % | 2.7 % | 50% RH; ISO 62 | |||
| 9.5 % | 9.5 % | Saturation; ISO 62 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | 121; ISO 527 | ||
| 80.0 MPa | 11600 psi | 23; ISO 527 | |||
| 136 MPa | 19700 psi | -40; ISO 527 | |||
| Elongation at Break | 25 % | 25 % | ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 | ||
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527 | ||
| Flexural Strength | 82.0 MPa | 11900 psi | ISO 178 | ||
| Charpy Impact, Notched | 0.350 J/cm2 | 1.67 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 285 °C | 464 - 545 °F | |||
| Mold Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | >= 0.15 % | >= 0.15 % | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| Descriptive Properties | |||||
| Commercial Status | North America | ||||