- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 5.0
- 缺口沖擊強度: 8.5
- 拉伸強度 [MPa]: 111.0
- 彎曲模量 [MPa]: 7.30
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |||
| Density | 1.35 g/cc | 0.0488 lb/in3 | ISO 1183 | ||
| Water Absorption | 5.0 - 6.0 % | 5.0 - 6.0 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | >= 1.3 % | >= 1.3 % | 50% RH; ISO 62 | ||
| 1.1 - 1.5 % | 1.1 - 1.5 % | 23°C; 50% RH; ISO 62 | |||
| >= 5.5 % | >= 5.5 % | Saturation; ISO 62 | |||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0039 cm/cm | 0.0039 in/in | restricted | ||
| Linear Mold Shrinkage, Flow | 0.0045 cm/cm | 0.0045 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 111 MPa @Temperature 80.0 °C | 16100 psi @Temperature 176 °F | ISO 527 | ||
| 185 MPa @Temperature 23.0 °C | 26800 psi @Temperature 73.4 °F | 50 mm/min; ISO 527-1/-2 | |||
| 214 MPa @Temperature -40.0 °C | 31000 psi @Temperature -40.0 °F | ISO 527 | |||
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 9.00 GPa | 1310 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 7.30 GPa | 1060 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 8.50 kJ/m2 @Temperature 23.0 °C | 4.04 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 6.00 J/cm2 @Temperature -30.0 °C | 28.6 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | ||
| 8.00 J/cm2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.850 J/cm2 @Temperature -30.0 °C | 4.04 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | ||
| 1.10 J/cm2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 4.3 @Frequency 1.00 Hz | 4.3 @Frequency 1.00 Hz | IEC 60250 | ||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.030 @Frequency 1.00e+6 Hz | 0.030 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.500 - 0.600 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.278 - 0.333 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.250 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.139 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 160 °C | 320 °F | for 50% loss of tensile strength after 5000hr | |||
| 270 °C | 518 °F | ||||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 350 °C | >= 662 °F | |||
| UL RTI, Electrical | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical with Impact | 115 °C @Thickness 1.50 mm | 239 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | 746B | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Zone 1 | 300 °C | 572 °F | Feed Zone | ||
| Zone 2 | 310 °C | 590 °F | Compression | ||
| Zone 3 | 320 °C | 608 °F | Metering-zone | ||
| Zone 4 | 320 °C | 608 °F | Nozzle | ||
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | ||
| 320 °C | 608 °F | Optimal | |||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection-molding | ||
| 100 °C | 212 °F | Optimal | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 8 hour | 8 hour | |||
| Moisture Content | <= 0.030 % | <= 0.030 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Commercial Status | Europe and North America | ||||
| Ignition Temperature | >470°C | ASTM D1929 | |||