- 熔體流動速率 [g/10min]: 116.45
- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 6.9
- 缺口沖擊強(qiáng)度: 8.0
- 拉伸強(qiáng)度 [MPa]: 50.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 | ||
| Water Absorption | 6.9 - 7.5 % | 6.9 - 7.5 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.1 - 2.5 % | 2.1 - 2.5 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 123 | 123 | ISO 307 | ||
| Melt Flow | 116.45 g/10 min @Load 5.00 kg, Temperature 275 °C | 116.45 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 2.7 % | 2.7 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 8.50 GPa | 1230 ksi | ISO 527-1/-2 | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 4.00 J/cm2 @Temperature -30.0 °C | 19.0 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 4.50 J/cm2 @Temperature 23.0 °C | 21.4 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.550 J/cm2 @Temperature -30.0 °C | 2.62 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.9 @Frequency 1.00 Hz | 3.9 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.600 - 1.10 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.333 - 0.611 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.340 - 0.380 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.189 - 0.211 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 180 °C | 356 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | BK 23210 | ||||
| Commercial Status | Europe | ||||