- 熔體流動速率 [g/10min]: 12.6
- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 4.7
- 缺口沖擊強度: 14.0
- 拉伸強度 [MPa]: 165.0
- 彎曲模量 [MPa]: 9.50
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ISO 1183 | ||
| Water Absorption | 4.7 - 5.3 % | 4.7 - 5.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.4 - 1.8 % | 1.4 - 1.8 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 160 | 160 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | restricted | ||
| Melt Flow | 12.6 g/10 min @Load 5.00 kg, Temperature 275 °C | 12.6 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 84.0 MPa @Load 36.5 kg, Time 30.0 sec | 12200 psi @Load 80.5 lb, Time 0.00833 hour | ISO 2039-1 | ||
| Tensile Strength, Yield | 165 MPa | 23900 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 4.6 % | 4.6 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 11.6 GPa | 1680 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 250 MPa | 36300 psi | at max force; ISO 178 | ||
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 14.0 kJ/m2 @Temperature -30.0 °C | 6.66 ft-lb/in2 @Temperature -22.0 °F | ISO 180/A | ||
| 22.0 kJ/m2 @Temperature 23.0 °C | 10.5 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | |||
| Charpy Impact Unnotched | 10.5 J/cm2 @Temperature -30.0 °C | 50.0 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 11.0 J/cm2 @Temperature 23.0 °C | 52.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.50 J/cm2 @Temperature -30.0 °C | 7.14 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 2.40 J/cm2 @Temperature 23.0 °C | 11.4 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1.00 Hz | 4.0 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.100 - 0.200 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.0556 - 0.111 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.500 - 0.600 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.278 - 0.333 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 180 °C | 356 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 260 °C | 500 °F | Feed Zone | ||
| Zone 2 | 270 °C | 518 °F | Compression | ||
| Zone 3 | 280 °C | 536 °F | Metering-zone | ||
| Zone 4 | 280 °C | 536 °F | Nozzle | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| 280 °C | 536 °F | Optimal | |||
| Mold Temperature | 80.0 °C | 176 °F | Optimal | ||
| 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 20560 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D129 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||