- 熔體流動(dòng)速率 [g/10min]: 12.6
- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 4.7
- 拉伸強(qiáng)度 [MPa]: 115.0
- 彎曲模量 [MPa]: 6.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ISO 1183 | ||
| Water Absorption | 4.7 - 5.3 % | 4.7 - 5.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.4 - 1.8 % | 1.4 - 1.8 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 160 | 160 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | restricted | ||
| Melt Flow | 12.6 g/10 min @Load 5.00 kg, Temperature 275 °C | 12.6 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 84.0 MPa @Load 36.5 kg, Time 30.0 sec | 12200 psi @Load 80.5 lb, Time 0.00833 hour | ISO 2039-1 | ||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 9.5 % | 9.5 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 6.70 GPa | 972 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 155 MPa | 22500 psi | at max force; ISO 178 | ||
| Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 13.0 J/cm2 @Temperature 23.0 °C | 61.9 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 4.00 J/cm2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.3 @Frequency 1.00 Hz | 5.3 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.13 @Frequency 1.00e+6 Hz | 0.13 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 180 °C | 356 °F | |||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 260 °C | 500 °F | Feed Zone | ||
| Zone 2 | 270 °C | 518 °F | Compression | ||
| Zone 3 | 280 °C | 536 °F | Metering-zone | ||
| Zone 4 | 280 °C | 536 °F | Nozzle | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| 280 °C | 536 °F | Optimal | |||
| Mold Temperature | 80.0 °C | 176 °F | Optimal | ||
| 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 20560 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D129 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||