- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 6.5
- 拉伸強度 [MPa]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.450 - 0.800 g/cc | 0.0163 - 0.0289 lb/in3 | |||
| Density | 1.16 g/cc | 0.0419 lb/in3 | ISO 1183 | ||
| Water Absorption | 6.5 - 7.5 % | 6.5 - 7.5 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.6 - 2.0 % | 1.6 - 2.0 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | restricted | ||
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Break | <= 11.5 % | <= 11.5 % | Nominal, 50mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 3.20 GPa | 464 ksi | ISO 527-1/-2 | ||
| Tensile Creep Modulus, 1000 hours | 2300 MPa @Strain <=0.500 % | 334000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1.00 Hz | 4.0 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.040 @Frequency 1.00e+6 Hz | 0.040 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 110 °C | 230 °F | for 50% loss of tensile strength after 20000hr | ||
| 130 °C | 266 °F | for 50% loss of tensile strength after 5000hr | |||
| 250 °C | 482 °F | ||||
| Decomposition Temperature | >= 350 °C | >= 662 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 300 °C | 572 °F | Feed Zone | ||
| Zone 2 | 310 °C | 590 °F | Compression | ||
| Zone 3 | 315 °C | 599 °F | Metering-zone | ||
| Zone 4 | 315 °C | 599 °F | Nozzle | ||
| Melt Temperature | 315 °C | 599 °F | Optimal | ||
| 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | |||
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | Injection-molding | ||
| 90.0 °C | 194 °F | Optimal | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 8 hour | 8 hour | |||
| Moisture Content | <= 0.030 % | <= 0.030 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 00464 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >470°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||