- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.9
- 彎曲強度 [MPa]: 67.0
- 彎曲模量 [MPa]: 3.68
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in3 | dry; ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.7 % | 5.7 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 67.0 MPa | 9720 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 14 % | 14 % | 5mm/min; ISO 527 | ||
| 14 % | 14 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 4.16 GPa | 603 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO Data | ||
| Flexural Modulus | 3.68 GPa | 534 ksi | ISO Data | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||