- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.9
- 彎曲強度 [MPa]: 90.0
- 彎曲模量 [MPa]: 4.83
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | Melt; ISO 1183 | ||
| 1.34 g/cc | 0.0484 lb/in3 | dry; ISO 1183 | |||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.5 % | 5.5 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 6.0 % | 6.0 % | 5mm/min; ISO 527 | ||
| 6.0 % | 6.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 4.61 GPa | 669 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 120 MPa | 17400 psi | ISO Data | ||
| 124 MPa | 18000 psi | ASTM Test | |||
| 90.0 MPa @Temperature 120 °C | 13100 psi @Temperature 248 °F | ASTM Test | |||
| 100 MPa @Temperature 93.0 °C | 14500 psi @Temperature 199 °F | ASTM Test | |||
| 110 MPa @Temperature 65.0 °C | 16000 psi @Temperature 149 °F | ASTM Test | |||
| 297 MPa @Temperature -40.0 °C | 43100 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 4.83 GPa | 701 ksi | ASTM Test | ||
| 5.03 GPa | 730 ksi | ISO Data | |||
| 2.97 GPa @Temperature 120 °C | 431 ksi @Temperature 248 °F | ASTM Test | |||
| 3.25 GPa @Temperature 93.0 °C | 471 ksi @Temperature 199 °F | ASTM Test | |||
| 3.29 GPa @Temperature 65.0 °C | 477 ksi @Temperature 149 °F | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.958 J/g-°C | 0.4680 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||